Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.18 g/cm³ Show Supplier Material materials with Density of 1.18 g/cm³ | ISO1183 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 3 GPa Show Supplier Material materials with Elastic modulus of 3 GPa | ISO527 |
Elongation | 23.0 °C | 50 % Show Supplier Material materials with Elongation of 50 % | ISO527 |
Flexural modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Flexural modulus of 2.7 GPa | ISO178 |
Flexural strength | 23.0 °C | 90 MPa Show Supplier Material materials with Flexural strength of 90 MPa | ISO178 |
Impact strength, Charpy notched | -30.0 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO179 |
23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO179 | |
Tensile strength | 23.0 °C | 85 MPa Show Supplier Material materials with Tensile strength of 85 MPa | ISO527 |
Thermal
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 130 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 130 °C | ISO75 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Oil cup, Preservative film | |
| Processing methods | Drying Temperature: 70-80°C, Drying Time: 6-8 hr, Rear Temperature: 230°C, Middle Temperature: 250°C, Front Temperature: 260°C, Nozzle Temperature: 270°C, Mold Temperature: 80-100°C, Injection Pressure: 70-100 MPa | |