General
Property | Value |
---|---|
Bound AN Content | 28.0 % Show Supplier Material materials with Bound AN Content of 28.0 % |
Density | 0.98 g/cm³ Show Supplier Material materials with Density of 0.98 g/cm³ |
Volatile share | 0.2 % Show Supplier Material materials with Volatile share of 0.2 % |
Mechanical
Property | Value | Testing Standard | Comment |
---|---|---|---|
Elongation | 435 % Show Supplier Material materials with Elongation of 435 % | ASTM D412 | 145°C×50min. Cured |
Modulus at 300% elongation | 0.019 GPa Show Supplier Material materials with Modulus at 300% elongation of 0.019 GPa | ASTM D412 | 145°C×50min. Cured |
Tensile strength | 290 MPa Show Supplier Material materials with Tensile strength of 290 MPa | ASTM D412 | 145°C×50min. Cured |
Thermal
Property | Value |
---|---|
Ash content | 0.5 % Show Supplier Material materials with Ash content of 0.5 % |
Rheological Properties
Property | Value | Comment |
---|---|---|
Mooney viscosity | 75 MU Show Supplier Material materials with Mooney viscosity of 75 MU | ML1+4 and 100°C (milled) |
Technological properties
Property | ||
---|---|---|
Application areas | NBR 2875 is preferably uesd for industrial and automotive hoses and many rubber parts such as roller, gasket and o-rings. And also, it can be used for foam insulation application due to excellent elasticity and good flexibility in low temperature. | |
Color | Light Tan | |
Other | Shelf Life : 18 months from date of production atb room temperatures not exceeding 30°C under belowed storage condition (Retest critical parameters like MV and others after the expiry of shelf life). Storage condition: NBR should be stored in warehouse to be protected from sunlight, heat, moisture and foreign materials. | |
Packaging size | Bale Weight: 35kg Bale wrapping film: LDPE | |
Processing history | Polymerization: Cold Emulsion | |
Processing methods | Recipe (ASTM D3187): NBR 2875: 100 phr HAF(IRB #8): 40 ZnO: 3.0 Stearic Acid: 1.0 TBBS: 0.7 Sulfur: 1.5 Total: 146.2 | |
Stabilizer | Non-Staining |