Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.81 g/cm³ Show Supplier Material materials with Density of 8.81 g/cm³ |
Dimension
Property | Value |
---|---|
Thickness | 0.05 - 0.38 mm Show Supplier Material materials with Thickness of 0.05 - 0.38 mm |
Width | 1.27 - 406.5 mm Show Supplier Material materials with Width of 1.27 - 406.5 mm |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Bendability 90°, bw | 23.0 °C | 5 [-] Show Supplier Material materials with Bendability 90°, bw of 5 [-] | >10mm (2 for <10mm) |
Bendability 90°, gw | 23.0 °C | 5 [-] Show Supplier Material materials with Bendability 90°, gw of 5 [-] | >10mm (2 for <10mm) |
Elastic modulus | 23.0 °C | 138 GPa Show Supplier Material materials with Elastic modulus of 138 GPa | |
Elongation | 23.0 °C | 1 % Show Supplier Material materials with Elongation of 1 % | in 25mm |
Fatigue strength | 23.0 °C | 580 - 685 MPa Show Supplier Material materials with Fatigue strength of 580 - 685 MPa | 10⁸ cycles R=0 (Unidirectional) |
Hardness, Vickers | 23.0 °C | 280 - 340 [-] Show Supplier Material materials with Hardness, Vickers of 280 - 340 [-] | |
Tensile strength | 23.0 °C | 950 - 1090 MPa Show Supplier Material materials with Tensile strength of 950 - 1090 MPa | |
Yield strength Rp0.2 | 23.0 °C | 930 - 1055 MPa Show Supplier Material materials with Yield strength Rp0.2 of 930 - 1055 MPa |
Thermal
Property | Value |
---|---|
Melting point | 1030 °C Show Supplier Material materials with Melting point of 1030 °C |
Electrical
Property | Value | Comment |
---|---|---|
Specific Electrical conductivity | 44 % IACS Show Supplier Material materials with Specific Electrical conductivity of 44 % IACS | nominal value |
Chemical properties
Property | Value |
---|---|
Beryllium | 0.15 - 0.5 % Show Supplier Material materials with Beryllium of 0.15 - 0.5 % |
Copper | Balance |
Nickel | 1 - 1.4 % Show Supplier Material materials with Nickel of 1 - 1.4 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications include power contacts and burn-in and test socket contacts. |