S-200-F C Beryllium Structural grades

Alternative and trade names
S-200-F C
Want to keep this datasheet? Save it now in your required format

Description

Cold isostatically pressed, sintered 98.5% beryllium. While the tensile properties are lower than other grades of beryllium, the modulus and thermal properties are the same.

Related Standards

This material data has been provided by Materion Brush GmbH.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Bulk density

23.0 °C

1.84 g/cm³

Show Supplier Material materials with Bulk density of 1.84 g/cm³

for BeO amount of 1.5%

Grain size

25 μm

Show Supplier Material materials with Grain size of 25 μm

max.

Mechanical

PropertyTemperatureValue

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

Tensile strength

23.0 °C

262 MPa

Show Supplier Material materials with Tensile strength of 262 MPa

Yield strength Rp0.2

23.0 °C

172 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 172 MPa

Chemical properties

PropertyValueComment

Aluminium

0.1 %

Show Supplier Material materials with Aluminium of 0.1 %

max.

Beryllium

98.5 %

Show Supplier Material materials with Beryllium of 98.5 %

min., BeO: 1.5% max

Carbon

0.15 %

Show Supplier Material materials with Carbon of 0.15 %

max.

Iron

0.13 %

Show Supplier Material materials with Iron of 0.13 %

max.

Magnesium

0.08 %

Show Supplier Material materials with Magnesium of 0.08 %

max.

Other

0.04 %

Show Supplier Material materials with Other of 0.04 %

max., other metallic impurities each

Silicon

0.06 %

Show Supplier Material materials with Silicon of 0.06 %

max.

Technological properties

Property
Application areas

Intelligence, surveillance and reconnaissance (ISR) systems, Electro-optical infrared (EO/IR) & targeting systems, Airborne early warning & control systems (AEW&C), Surveillance, reconnaissance and targeting (SRT), Size, weight and power (SWaP) replacement systems, Semiconductor capital equipment, Space-based systems and components, James Webb Space Telescope support structure

Processing history

This standard grade is produced from beryllium powder consolidated by cold isostatic pressing (CIP) and sintering.