General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 9 g/cm³ Show Supplier Material materials with Density of 9 g/cm³ |
Dimension
Property | Value |
---|---|
Diameter | 15.1 - 228.6 mm Show Supplier Material materials with Diameter of 15.1 - 228.6 mm |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 144 GPa Show Supplier Material materials with Elastic modulus of 144 GPa |
Elongation | 23.0 °C | 6 - 10 % Show Supplier Material materials with Elongation of 6 - 10 % |
Hardness, Rockwell C | 23.0 °C | 30 [-] Show Supplier Material materials with Hardness, Rockwell C of 30 [-] |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Supplier Material materials with Poisson's ratio of 0.33 [-] |
Tensile strength | 23.0 °C | 875 - 910 MPa Show Supplier Material materials with Tensile strength of 875 - 910 MPa |
Yield strength Rp0.2 | 23.0 °C | 760 MPa Show Supplier Material materials with Yield strength Rp0.2 of 760 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.64E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.64E-5 1/K |
Thermal conductivity | 23.0 °C | 38 W/(m·K) Show Supplier Material materials with Thermal conductivity of 38 W/(m·K) |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical conductivity | 23.0 °C | 4.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 4.00E+6 S/m | max. |
Specific Electrical conductivity | 7 % IACS Show Supplier Material materials with Specific Electrical conductivity of 7 % IACS | max. |
Magnetic
Property | Temperature | Value |
---|---|---|
Relative magnetic permeability | 23.0 °C | 1 [-] Show Supplier Material materials with Relative magnetic permeability of 1 [-] |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | ToughMet 3 AT alloy is used for bushings and bearings for commercial aircraft, high performance engines as well as mining, industrial and heavy equipment. It is also used to make oil and gas drilling hardware, including rotary steerable housings, kelly valve seats and pressure housings. | |
Surface Finish | Mill hardened finish |