General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 9 g/cm³ Show Supplier Material materials with Density of 9 g/cm³ |
Dimension
Property | Value |
---|---|
Outside diameter | 38 - 77 mm Show Supplier Material materials with Outside diameter of 38 - 77 mm |
Wall thickness | <10, >10 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 144 GPa Show Supplier Material materials with Elastic modulus of 144 GPa | |
Elongation | 23.0 °C | 5 % Show Supplier Material materials with Elongation of 5 % | in 4D |
Hardness, Rockwell C | 23.0 °C | 36 [-] Show Supplier Material materials with Hardness, Rockwell C of 36 [-] | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Supplier Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 1090 MPa Show Supplier Material materials with Tensile strength of 1090 MPa | |
Yield strength Rp0.2 | 23.0 °C | 1035 MPa Show Supplier Material materials with Yield strength Rp0.2 of 1035 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.64E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.64E-5 1/K |
Thermal conductivity | 23.0 °C | 38 W/(m·K) Show Supplier Material materials with Thermal conductivity of 38 W/(m·K) |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical conductivity | 23.0 °C | 4.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 4.00E+6 S/m | max. |
Specific Electrical conductivity | 7 % IACS Show Supplier Material materials with Specific Electrical conductivity of 7 % IACS | max. |
Magnetic
Property | Temperature | Value |
---|---|---|
Relative magnetic permeability | 23.0 °C | 1 [-] Show Supplier Material materials with Relative magnetic permeability of 1 [-] |
Technological properties
Property | ||
---|---|---|
Application areas | ToughMet 3 TS alloy tempers are commonly used in the oil and gas industry, oil & gas production via our sucker rod couplings and in commercial aircraft. |