General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.27 g/cm³ Show Supplier Material materials with Density of 8.27 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Bendability 90°, bw | 23.0 °C | 0 [-] Show Supplier Material materials with Bendability 90°, bw of 0 [-] | |
Bendability 90°, gw | 23.0 °C | 0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | |
Elastic modulus | 23.0 °C | 195 - 210 GPa Show Supplier Material materials with Elastic modulus of 195 - 210 GPa | |
Elongation | 23.0 °C | 14 % Show Supplier Material materials with Elongation of 14 % | min., for strip thicker than 0.10 mm |
Tensile strength | 23.0 °C | 1070 - 1240 MPa Show Supplier Material materials with Tensile strength of 1070 - 1240 MPa | |
Yield strength Rp0.2 | 23.0 °C | 690 - 860 MPa Show Supplier Material materials with Yield strength Rp0.2 of 690 - 860 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.45E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.45E-5 1/K |
Melting point | 1195 - 1325 °C Show Supplier Material materials with Melting point of 1195 - 1325 °C | |
Thermal conductivity | 23.0 °C | 48 W/(m·K) Show Supplier Material materials with Thermal conductivity of 48 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 3.45E-7 Ω·m Show Supplier Material materials with Electrical resistivity of 3.45E-7 Ω·m |
Specific Electrical conductivity | 5 % IACS Show Supplier Material materials with Specific Electrical conductivity of 5 % IACS |
Technological properties
Property | ||
---|---|---|
Application areas | Some applications for this alloy are Belleville washers for fire protection sprinkler heads, thermostats, bellows, diaphragms, connectors and burn-in and test sockets electrical /electronic systems. | |
Plating | Alloy 360 strip when properly cleaned exhibits surface chemistry characteristics similar to other commercial nickel base alloys. Techniques and procedures for plating and joining commercial nickel base alloys can be used on nickel beryllium. | |
Workability | Excellent - Used for deep-drawn and severely cupped or formed parts; can be bent flat through 180° angle in any direction |