General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.41 g/cm³ Show Supplier Material materials with Density of 8.41 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 131 GPa Show Supplier Material materials with Elastic modulus of 131 GPa |
Elongation | 23.0 °C | 35 - 60 % Show Supplier Material materials with Elongation of 35 - 60 % |
Hardness, Rockwell B | 23.0 °C | 45 - 85 [-] Show Supplier Material materials with Hardness, Rockwell B of 45 - 85 [-] |
Tensile strength | 23.0 °C | 410 - 590 MPa Show Supplier Material materials with Tensile strength of 410 - 590 MPa |
Yield strength Rp0.2 | 23.0 °C | 130 - 280 MPa Show Supplier Material materials with Yield strength Rp0.2 of 130 - 280 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K |
Melting point | 870 °C Show Supplier Material materials with Melting point of 870 °C | |
Thermal conductivity | 23.0 °C | 105 W/(m·K) Show Supplier Material materials with Thermal conductivity of 105 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 6.2E-6 - 7.89E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 6.2E-6 - 7.89E-6 Ω·m |
Specific Electrical conductivity | 22 - 28 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 - 28 % IACS |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Beryllium | 1.6 - 1.85 % Show Supplier Material materials with Beryllium of 1.6 - 1.85 % | ||
Cobalt | 0.2 % Show Supplier Material materials with Cobalt of 0.2 % | min. Nickel + Cobalt | |
Copper | Balance | ||
Iron | 0.6 % Show Supplier Material materials with Iron of 0.6 % | max., Nickel + Cobalt + Iron | |
Nickel | 0.2 % Show Supplier Material materials with Nickel of 0.2 % | min. Nickel + Cobalt |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications for parts finished by forging or extrusion of these alloys include undersea instrument and repeater housings, generator rings, and resistance welding components. |