General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.69 g/cm³ Show Supplier Material materials with Density of 8.69 g/cm³ |
Dimension
Property | Value | Comment |
---|---|---|
Outside diameter | 114.3 mm Show Supplier Material materials with Outside diameter of 114.3 mm | max., other sizes are available upon request |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 130 GPa Show Supplier Material materials with Elastic modulus of 130 GPa | |
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | |
Hardness, HBW | 23.0 °C | 265 [-] Show Supplier Material materials with Hardness, HBW of 265 [-] | |
Hardness, Rockwell C | 23.0 °C | 27 [-] Show Supplier Material materials with Hardness, Rockwell C of 27 [-] | HRC values converted per ASTM-E-140, Table 1. |
Tensile strength | 23.0 °C | 860 MPa Show Supplier Material materials with Tensile strength of 860 MPa | |
Yield strength Rp0.2 | 23.0 °C | 790 MPa Show Supplier Material materials with Yield strength Rp0.2 of 790 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K |
Thermal conductivity | 25.0 °C | 155 W/(m·K) Show Supplier Material materials with Thermal conductivity of 155 W/(m·K) |
250.0 °C | 215 W/(m·K) Show Supplier Material materials with Thermal conductivity of 215 W/(m·K) | |
Chemical properties
Property | Value |
---|---|
Chromium | 0.6 - 1.2 % Show Supplier Material materials with Chromium of 0.6 - 1.2 % |
Copper | Balance |
Nickel | 6.4 - 6.7 % Show Supplier Material materials with Nickel of 6.4 - 6.7 % |
Silicon | 1.5 - 2.5 % Show Supplier Material materials with Silicon of 1.5 - 2.5 % |
Technological properties
Property | ||
---|---|---|
Application areas | Applications include valve seats, valve guides, piston rings and plain bearings, where PerforMet provides long life while efficiently removing heat from critical engine components. |