MoldMAX V®

Alternative and trade names
MoldMAX V®

Want to keep this datasheet? Save it now in your required format

Description

Materion Performance Alloys’ MoldMAX V (MMV) Alloy is a high conductivity, moderately high strength, copper nickel silicon chromium alloy.

This material data has been provided by Materion Brush GmbH.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value
Density	23.0 °C	8.69 g/cm³ Show Supplier Material materials with Density of 8.69 g/cm³

Dimension

Property	Value
Diameter	12.5 - 63.5 mm Show Supplier Material materials with Diameter of 12.5 - 63.5 mm

Mechanical

Property	Temperature	Value	Comment
Charpy impact energy	23.0 °C	7 J Show Supplier Material materials with Charpy impact energy of 7 J
Elastic modulus	23.0 °C	130 GPa Show Supplier Material materials with Elastic modulus of 130 GPa
Elongation	23.0 °C	5 - 7 % Show Supplier Material materials with Elongation of 5 - 7 %
Fatigue strength	23.0 °C	275 MPa Show Supplier Material materials with Fatigue strength of 275 MPa	10⁷ cycles, R=-1
Hardness, HBW	23.0 °C	250 - 265 [-] Show Supplier Material materials with Hardness, HBW of 250 - 265 [-]
Hardness, Rockwell C	23.0 °C	25 - 27 [-] Show Supplier Material materials with Hardness, Rockwell C of 25 - 27 [-]	HRC values converted per ASTM-E-140, Table 1.
Tensile strength	23.0 °C	790 - 860 MPa Show Supplier Material materials with Tensile strength of 790 - 860 MPa
Yield strength Rp0.2	23.0 °C	690 - 790 MPa Show Supplier Material materials with Yield strength Rp0.2 of 690 - 790 MPa

Thermal

Property	Temperature	Value
Coefficient of thermal expansion	23.0 °C	1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K
Melting point		980 °C Show Supplier Material materials with Melting point of 980 °C
Specific heat capacity	100.0 °C	410 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 410 J/(kg·K)
Thermal conductivity	100.0 °C	160 W/(m·K) Show Supplier Material materials with Thermal conductivity of 160 W/(m·K)

Chemical properties

Property	Value
Chromium	0.6 - 1.2 % Show Supplier Material materials with Chromium of 0.6 - 1.2 %
Copper	Balance
Nickel	6.4 - 7.6 % Show Supplier Material materials with Nickel of 6.4 - 7.6 %
Silicon	1.5 - 2.5 % Show Supplier Material materials with Silicon of 1.5 - 2.5 %

Technological properties

Property
Application areas	Applications include injection mold and blow mold cores and cavities.

MoldMAX V®

Description

Ashby charts

Applications

Materials by this supplier

Properties