Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.83 g/cm³ Show Supplier Material materials with Density of 8.83 g/cm³ |
Dimension
| Property | Value | Comment |
|---|---|---|
Length | 91000 mm Show Supplier Material materials with Length of 91000 mm | max. Rod and Bar |
Outside diameter | 0.76 - 76 mm Show Supplier Material materials with Outside diameter of 0.76 - 76 mm | Rod |
Thickness | 0.76 - 76 mm Show Supplier Material materials with Thickness of 0.76 - 76 mm | Bar |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 138 GPa Show Supplier Material materials with Elastic modulus of 138 GPa |
Elongation | 23.0 °C | 10 - 15 % Show Supplier Material materials with Elongation of 10 - 15 % |
Tensile strength | 23.0 °C | 480 - 550 MPa Show Supplier Material materials with Tensile strength of 480 - 550 MPa |
Yield strength Rp0.2 | 23.0 °C | 340 - 520 MPa Show Supplier Material materials with Yield strength Rp0.2 of 340 - 520 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.76E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.76E-5 1/K |
Melting point | 1040 °C Show Supplier Material materials with Melting point of 1040 °C | |
Thermal conductivity | 23.0 °C | 240 W/(m·K) Show Supplier Material materials with Thermal conductivity of 240 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 2.9E-6 - 3.8E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 2.9E-6 - 3.8E-6 Ω·m |
Specific Electrical conductivity | 45 - 60 % IACS Show Supplier Material materials with Specific Electrical conductivity of 45 - 60 % IACS |
Chemical properties
| Property | Value |
|---|---|
Beryllium | 0.2 - 0.6 % Show Supplier Material materials with Beryllium of 0.2 - 0.6 % |
Copper | Balance |
Nickel | 1.4 - 2.2 % Show Supplier Material materials with Nickel of 1.4 - 2.2 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications include dies casting plunger tips and dies for steel extrusion. | |