General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.83 g/cm³ Show Supplier Material materials with Density of 8.83 g/cm³ |
Dimension
Property | Value | Comment |
---|---|---|
Length | 91000 mm Show Supplier Material materials with Length of 91000 mm | max. Rod and Bar |
Outside diameter | 0.76 - 254 mm Show Supplier Material materials with Outside diameter of 0.76 - 254 mm | Rod |
Thickness | 0.76 - 254 mm Show Supplier Material materials with Thickness of 0.76 - 254 mm | Bar |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 138 GPa Show Supplier Material materials with Elastic modulus of 138 GPa |
Elongation | 23.0 °C | 20 - 35 % Show Supplier Material materials with Elongation of 20 - 35 % |
Tensile strength | 23.0 °C | 240 - 380 MPa Show Supplier Material materials with Tensile strength of 240 - 380 MPa |
Yield strength Rp0.2 | 23.0 °C | 70 - 210 MPa Show Supplier Material materials with Yield strength Rp0.2 of 70 - 210 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.76E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.76E-5 1/K |
Melting point | 1010 °C Show Supplier Material materials with Melting point of 1010 °C | |
Thermal conductivity | 23.0 °C | 200 W/(m·K) Show Supplier Material materials with Thermal conductivity of 200 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 2.9E-6 - 3.8E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 2.9E-6 - 3.8E-6 Ω·m |
Specific Electrical conductivity | 45 - 60 % IACS Show Supplier Material materials with Specific Electrical conductivity of 45 - 60 % IACS |
Chemical properties
Property | Value |
---|---|
Beryllium | 0.4 - 0.7 % Show Supplier Material materials with Beryllium of 0.4 - 0.7 % |
Cobalt | 2.4 - 2.7 % Show Supplier Material materials with Cobalt of 2.4 - 2.7 % |
Copper | Balance |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications include dies casting plunger tips and dies for steel extrusion. |