Hytrel® HTR8745 BK320

Alternative and trade names
TPC-ET
Want to keep this datasheet? Save it now in your required format

Description

Hytrel® HTR8745 BK320 is a 45 Shore D, Heat Stabilized, Black, High Performance High Flow Polyester Elastomer with Excellent Fatigue Resistance Developed for Blow Molding

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.14 g/cm³

Show Material materials with Density of 1.14 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.08 GPa

Show Material materials with Elastic modulus of 0.08 GPa

ISO 527-1/-2

Elongation

23.0 °C

500 %

Show Material materials with Elongation of 500 %

ISO 527-1/-2

Hardness, Shore D

23.0 °C

45 [-]

Show Material materials with Hardness, Shore D of 45 [-]

max., ISO 7619-1

Tear strength

23.0 °C

120 kN/m

Show Material materials with Tear strength of 120 kN/m

ISO 34-1

Tear strength, transverse

23.0 °C

120 kN/m

Show Material materials with Tear strength, transverse of 120 kN/m

ISO 34-1

Tensile strength

23.0 °C

34 MPa

Show Material materials with Tensile strength of 34 MPa

ISO 527-1/-2

Impact strength, Charpy notched

No Break @ -6,-40°C, ISO 179/1eA

Impact strength, Izod unnotched

No Break @ -40°C,ISO 180/1A

Thermal

PropertyValueComment

Melting point

203 °C

Show Material materials with Melting point of 203 °C

ISO 11357-1/-3 | 18°F/min

Vicat softening temperature

160 °C

Show Material materials with Vicat softening temperature of 160 °C

ISO 306 | 90°F, 2 lbf

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

6.5 g/10min

Show Material materials with Melt mass-flow rate of 6.5 g/10min

ISO 1133 | 230°C/10kg

Shrinkage, transverse

23.0 °C

1.8 %

Show Material materials with Shrinkage, transverse of 1.8 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C