Carbon Chopped Fibre (C006560)

Alternative and trade names
Grafil 34-700 carbon fiber
Want to keep this datasheet? Save it now in your required format

Description

Carbon - Chopped Fibre - C 006560 is a high strength, PAN based fiber

Related Standards

Ashby charts

See where Carbon Chopped Fibre (C006560) falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

1.8 g/cm³ at 23 °C

SRM 15 (typical fibre properties)

Yield 12K

Y12K

800 mg/m at 23 °C

SRM 13

Yield 24K

Y24K

1600 mg/m at 23 °C

SRM 13

Dimension

Diameter

d

6.999999999999999E-3 mm

Length

l

6 mm

fiber length

Mechanical

Compressive modulus

Ecomp

127 MPa at 23 °C

Show Carbon materials with Compressive modulus of 127 MPa at 23 °C

ASTM D3039

Compressive modulus, transverse

Ecomp,trans

10.2 MPa at 23 °C

Show Carbon materials with Compressive modulus, transverse of 10.2 MPa at 23 °C

ASTM D3039

Compressive strength

Rmc

1365 MPa at 23 °C

Show Carbon materials with Compressive strength of 1365 MPa at 23 °C

ASTM D3039

Compressive strength, transverse

Rs,trans

196 MPa at 23 °C

Show Carbon materials with Compressive strength, transverse of 196 MPa at 23 °C

ASTM D3039

Elastic modulus

E

137 GPa at 23 °C

Show Carbon materials with Elastic modulus of 137 GPa at 23 °C

ASTM D3039

Elastic modulus, transverse

E

9.2 GPa at 23 °C

Show Carbon materials with Elastic modulus, transverse of 9.2 GPa at 23 °C

ASTM D3039

Flexural modulus

Ebend

132 GPa at 23 °C

Show Carbon materials with Flexural modulus of 132 GPa at 23 °C

ASTM D790 (L/D=32, Vf=61%)

Flexural modulus, transverse

Ebend,trans

8.8 GPa at 23 °C

Show Carbon materials with Flexural modulus, transverse of 8.8 GPa at 23 °C

ASTM D790 (L/D=32, Vf=61%)

Flexural strength

σbend

1745 MPa at 23 °C

Show Carbon materials with Flexural strength of 1745 MPa at 23 °C

ASTM D790 (L/D=32, Vf=61%)

Flexural strength, transverse

σbendT

102 MPa at 23 °C

Show Carbon materials with Flexural strength, transverse of 102 MPa at 23 °C

ASTM D790 (L/D=32, Vf=61%)

Interlaminar shear strength

ILSS

97 MPa at 23 °C

Show Carbon materials with Interlaminar shear strength of 97 MPa at 23 °C

ASTM D2344 (L/D=4, Vf=59%)

Tensile strength

Rm

2572 MPa at 23 °C

Show Carbon materials with Tensile strength of 2572 MPa at 23 °C

ASTM D3039

Tensile strength, transverse

Rm,trans

81 MPa at 23 °C

Show Carbon materials with Tensile strength, transverse of 81 MPa at 23 °C

ASTM D3039

Tow tensile modulus

Etow

234 GPa at 23 °C

Show Carbon materials with Tow tensile modulus of 234 GPa at 23 °C

SRM 16 (typical fibre properties)

Tow tensile strength

Rm,two

4830 MPa at 23 °C

Show Carbon materials with Tow tensile strength of 4830 MPa at 23 °C

SRM 16 (typical fibre properties)

Technological properties

Processing history

Epoxy sized 1.2%

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.