EN 12163 Grade CuNi10Fe1Mn R280

View suppliers (4)
Want to keep this datasheet? Save it now in your required format

Description

CuNi10Fe1Mn (CW352H) is comparable to CuNi10Fe1Mn, mat. no. 2.0872, acc. to DIN 17664 : 1983-12. To the comparable DIN-mark applies: The material shows favorable specific strength values also at endurance loading and increased temperatures. Thermal conductivity of pure copper is strongly reduced by Ni, the electrical resistance strongly increases according to the Ni-content. Fe-addition increases the corrosion resistance. CuNi10Fe1Mn is resistant to seawater, alkaline saline solutions and non-oxidizing acids. warm forming: good cold forming: very good machinability: unfavorable hard soldering: very good soft soldering: very good gas-shielded welding: very good burnishing: good Application: For seawater pipilines, tubes and plates for all types of tubular heat-exchanger (condenser, cooler, seawater evaporators, high pressure feeder water heater) on ships, in power plants, seawater desalination plants, chemical and sugar factories.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.9 g/cm³

Show Material materials with Density of 8.9 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-253.0 °C

153 GPa

Show Material materials with Elastic modulus of 153 GPa

-195.0 °C

148 GPa

Show Material materials with Elastic modulus of 148 GPa

-100.0 °C

142 GPa

Show Material materials with Elastic modulus of 142 GPa

20.0 °C

130 GPa

Show Material materials with Elastic modulus of 130 GPa

50.0 °C

129 GPa

Show Material materials with Elastic modulus of 129 GPa

100.0 °C

128 GPa

Show Material materials with Elastic modulus of 128 GPa

150.0 °C

127 GPa

Show Material materials with Elastic modulus of 127 GPa

200.0 °C

125 GPa

Show Material materials with Elastic modulus of 125 GPa

250.0 °C

122 GPa

Show Material materials with Elastic modulus of 122 GPa

300.0 °C

121 GPa

Show Material materials with Elastic modulus of 121 GPa

Elongation

20.0 °C

20 - 30 %

Show Material materials with Elongation of 20 - 30 %

Hardness, Vickers

20.0 °C

85 [-]

Show Material materials with Hardness, Vickers of 85 [-]

Tensile strength

20.0 °C

280 MPa

Show Material materials with Tensile strength of 280 MPa

Yield strength Rp0.2

20.0 °C

90 - 110 MPa

Show Material materials with Yield strength Rp0.2 of 90 - 110 MPa

Yield strength Rp1.0

20.0 °C

125 MPa

Show Material materials with Yield strength Rp1.0 of 125 MPa

50.0 °C

125 MPa

Show Material materials with Yield strength Rp1.0 of 125 MPa

100.0 °C

118 MPa

Show Material materials with Yield strength Rp1.0 of 118 MPa

150.0 °C

114 MPa

Show Material materials with Yield strength Rp1.0 of 114 MPa

200.0 °C

109 MPa

Show Material materials with Yield strength Rp1.0 of 109 MPa

250.0 °C

104 MPa

Show Material materials with Yield strength Rp1.0 of 104 MPa

300.0 °C

99 MPa

Show Material materials with Yield strength Rp1.0 of 99 MPa

Unlock all property charts

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.4E-5 - 1.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.4E-5 - 1.8E-5 1/K

Typical for Wrought Copper Nickel Grade

Melting point

915 - 1240 °C

Show Material materials with Melting point of 915 - 1240 °C

Typical for Wrought Copper Nickel Grade

Specific heat capacity

20.0 °C

380 J/(kg·K)

Show Material materials with Specific heat capacity of 380 J/(kg·K)

Thermal conductivity

20.0 °C

50.2 W/(m·K)

Show Material materials with Thermal conductivity of 50.2 W/(m·K)

Chemical properties

PropertyValue

Carbon

0.05 %

Show Material materials with Carbon of 0.05 %

Cobalt

0.1 %

Show Material materials with Cobalt of 0.1 %

Iron

1 - 2 %

Show Material materials with Iron of 1 - 2 %

Lead

0.02 %

Show Material materials with Lead of 0.02 %

Manganese

0.5 - 1 %

Show Material materials with Manganese of 0.5 - 1 %

Nickel

9 - 11 %

Show Material materials with Nickel of 9 - 11 %

Phosphorus

0.02 %

Show Material materials with Phosphorus of 0.02 %

Sulfur

0.05 %

Show Material materials with Sulfur of 0.05 %

Tin

0.03 %

Show Material materials with Tin of 0.03 %

Zinc

0.5 %

Show Material materials with Zinc of 0.5 %