General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.79 - 8.8 g/cm³ Show Material materials with Density of 8.79 - 8.8 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 124 GPa Show Material materials with Elastic modulus of 124 GPa |
100.0 °C | 123 GPa Show Material materials with Elastic modulus of 123 GPa | |
200.0 °C | 118 GPa Show Material materials with Elastic modulus of 118 GPa | |
300.0 °C | 113 GPa Show Material materials with Elastic modulus of 113 GPa | |
400.0 °C | 107 GPa Show Material materials with Elastic modulus of 107 GPa | |
500.0 °C | 98 GPa Show Material materials with Elastic modulus of 98 GPa | |
600.0 °C | 88 GPa Show Material materials with Elastic modulus of 88 GPa | |
700.0 °C | 78 GPa Show Material materials with Elastic modulus of 78 GPa | |
Elongation | 20.0 °C | 12 % Show Material materials with Elongation of 12 % |
Elongation A100 | 20.0 °C | 10 % Show Material materials with Elongation A100 of 10 % |
Elongation A11.3 | 20.0 °C | 11 % Show Material materials with Elongation A11.3 of 11 % |
Poisson's ratio | 20.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] |
Shear modulus | 20.0 °C | 46 GPa Show Material materials with Shear modulus of 46 GPa |
Tensile strength | 20.0 °C | 380 MPa Show Material materials with Tensile strength of 380 MPa |
Yield strength Rp0.2 | 20.0 °C | 280 - 350 MPa Show Material materials with Yield strength Rp0.2 of 280 - 350 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 200.0 °C | 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 376 - 377 J/(kg·K) Show Material materials with Specific heat capacity of 376 - 377 J/(kg·K) | |
100.0 °C | 398 J/(kg·K) Show Material materials with Specific heat capacity of 398 J/(kg·K) | ||
200.0 °C | 410 J/(kg·K) Show Material materials with Specific heat capacity of 410 J/(kg·K) | ||
300.0 °C | 419 J/(kg·K) Show Material materials with Specific heat capacity of 419 J/(kg·K) | ||
400.0 °C | 431 J/(kg·K) Show Material materials with Specific heat capacity of 431 J/(kg·K) | ||
500.0 °C | 444 J/(kg·K) Show Material materials with Specific heat capacity of 444 J/(kg·K) | ||
600.0 °C | 452 J/(kg·K) Show Material materials with Specific heat capacity of 452 J/(kg·K) | ||
700.0 °C | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 184 W/(m·K) Show Material materials with Thermal conductivity of 184 W/(m·K) | |
80.0 °C | 197 W/(m·K) Show Material materials with Thermal conductivity of 197 W/(m·K) | ||
120.0 °C | 209 W/(m·K) Show Material materials with Thermal conductivity of 209 W/(m·K) | ||
160.0 °C | 218 W/(m·K) Show Material materials with Thermal conductivity of 218 W/(m·K) | ||
200.0 °C | 226 W/(m·K) Show Material materials with Thermal conductivity of 226 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 2.47E+7 - 2.50E+7 S/m Show Material materials with Electrical conductivity of 2.47E+7 - 2.50E+7 S/m |
Electrical resistivity | 20.0 °C | 4.1E-8 Ω·m Show Material materials with Electrical resistivity of 4.1E-8 Ω·m |
Specific Electrical conductivity | 43 % IACS Show Material materials with Specific Electrical conductivity of 43 % IACS |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Copper | 89 - 91 % Show Material materials with Copper of 89 - 91 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 0.05 % Show Material materials with Lead of 0.05 % |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % |
Tin | 0.1 % Show Material materials with Tin of 0.1 % |