General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 8.35 - 8.4 g/cm³ Show Material materials with Density of 8.35 - 8.4 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20.0 °C | 112 GPa Show Material materials with Elastic modulus of 112 GPa |
Elongation | 20.0 °C | 15 - 20 % Show Material materials with Elongation of 15 - 20 % |
Elongation A10 | 20.0 °C | 16 % Show Material materials with Elongation A10 of 16 % |
Elongation A100 | 20.0 °C | 8 % Show Material materials with Elongation A100 of 8 % |
Elongation A11.3 | 20.0 °C | 10 % Show Material materials with Elongation A11.3 of 10 % |
Hardness, Vickers | 20.0 °C | 110 [-] Show Material materials with Hardness, Vickers of 110 [-] |
Shear modulus | 20.0 °C | 42 GPa Show Material materials with Shear modulus of 42 GPa |
Tensile strength | 20.0 °C | 400 MPa Show Material materials with Tensile strength of 400 MPa |
Yield strength Rp0.2 | 20.0 °C | 180 - 210 MPa Show Material materials with Yield strength Rp0.2 of 180 - 210 MPa |
100.0 °C | 200 MPa Show Material materials with Yield strength Rp0.2 of 200 MPa | |
150.0 °C | 190 MPa Show Material materials with Yield strength Rp0.2 of 190 MPa | |
200.0 °C | 180 MPa Show Material materials with Yield strength Rp0.2 of 180 MPa | |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C Show Material materials with Melting point of 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) Show Material materials with Specific heat capacity of 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 20.0 °C | 117 W/(m·K) Show Material materials with Thermal conductivity of 117 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.51E+7 S/m Show Material materials with Electrical conductivity of 1.51E+7 S/m |
Electrical resistivity | 20.0 °C | 6.6E-8 Ω·m Show Material materials with Electrical resistivity of 6.6E-8 Ω·m |
Chemical properties