EN 12166 Grade CuNi12Zn24 R800

Want to keep this datasheet? Save it now in your required format


Material CuNi12Zn24, mat. No. CW403J is an alloy of high strength and hardness. To the comparabel DIN-mark CuNi12Zn24, mat. No. 2.0730, acc. to DIN 17663 : 1983-12 applies: Strength is further increasable due to the high strain hardening capability. The material does not embrittle at low temperatures. Low electrical and thermal conductivity. The alloy is non-magnetic, corrosion resistance is better than for pure copper. Processing properties: warm forming: moderately cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: very good burnishing: very good Application: In electrical engineering and electronics for springs, contacts, membranes as well as in precision engineering and in equipment manufacturing. In food industry, for musical instruments, glasses frames, safety keys as well as in construction trade for paneling, show-cases and stairrails.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





20.0 °C

8.67 - 8.7 g/cm³

Show Material materials with Density of 8.67 - 8.7 g/cm³



Elastic modulus

20.0 °C

125 GPa

Show Material materials with Elastic modulus of 125 GPa

Poisson's ratio

20.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

20.0 °C

800 MPa

Show Material materials with Tensile strength of 800 MPa

Yield strength Rp0.2

20.0 °C

700 MPa

Show Material materials with Yield strength Rp0.2 of 700 MPa



Coefficient of thermal expansion

300.0 °C

1.65E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.65E-5 1/K

Melting point

875 - 1135 °C

Show Material materials with Melting point of 875 - 1135 °C

Typical for Wrought Copper Nickel Silver Grade

Specific heat capacity

20.0 °C

380 J/(kg·K)

Show Material materials with Specific heat capacity of 380 J/(kg·K)

Thermal conductivity

20.0 °C

42 W/(m·K)

Show Material materials with Thermal conductivity of 42 W/(m·K)



Electrical conductivity

20.0 °C

4.40E+6 S/m

Show Material materials with Electrical conductivity of 4.40E+6 S/m

Specific Electrical conductivity

8 % IACS

Show Material materials with Specific Electrical conductivity of 8 % IACS

Chemical properties



63 - 66 %

Show Material materials with Copper of 63 - 66 %


0.3 %

Show Material materials with Iron of 0.3 %


0.03 %

Show Material materials with Lead of 0.03 %


0.5 %

Show Material materials with Manganese of 0.5 %


11 - 13 %

Show Material materials with Nickel of 11 - 13 %


0.03 %

Show Material materials with Tin of 0.03 %