UNS C70250 boway

Alternative and trade names
boway 70250HS
Want to keep this datasheet? Save it now in your required format

Description

Ultra high strength combined with good electrical conductivity. Very good stress relaxation resistance.

Equivalent Materials

This material data has been provided by Ningbo Boway Alloy Material.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValue

Density

8.8 g/cm³

Show Supplier Material materials with Density of 8.8 g/cm³

Dimension

PropertyValue

Dimensions

Strip thickness 0.07 - 0.25 mm, other gauges on request. Strip width from 8.5 mm. Hot-dip tinned and electroplated strip available.

Mechanical

PropertyValueTesting StandardComment

Bendability 90°, bw

2.5 [-]

Show Supplier Material materials with Bendability 90°, bw of 2.5 [-]

EN ISO 7438

R840(TM08) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

Bendability 90°, gw

2 [-]

Show Supplier Material materials with Bendability 90°, gw of 2 [-]

EN ISO 7438

R840(TM08) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

Elastic modulus

130 GPa

Show Supplier Material materials with Elastic modulus of 130 GPa

Elongation

1 %

Show Supplier Material materials with Elongation of 1 %

min. | R840(TM08), A50

1 %

Show Supplier Material materials with Elongation of 1 %

min. | R900(TM10), A50

Hardness, Vickers

260 - 300 [-]

Show Supplier Material materials with Hardness, Vickers of 260 - 300 [-]

R840(TM08) | For reference only

270 - 330 [-]

Show Supplier Material materials with Hardness, Vickers of 270 - 330 [-]

R900(TM10) | For reference only

300 - 350 [-]

Show Supplier Material materials with Hardness, Vickers of 300 - 350 [-]

R1000(TM12) | For reference only

Poisson's ratio

0.33 [-]

Show Supplier Material materials with Poisson's ratio of 0.33 [-]

Tensile strength

840 - 920 MPa

Show Supplier Material materials with Tensile strength of 840 - 920 MPa

R840(TM08)

900 - 1000 MPa

Show Supplier Material materials with Tensile strength of 900 - 1000 MPa

R900(TM10)

Yield strength

810 MPa

Show Supplier Material materials with Yield strength of 810 MPa

min. | R840(TM08)

880 MPa

Show Supplier Material materials with Yield strength of 880 MPa

min. | R900(TM10)

950 MPa

Show Supplier Material materials with Yield strength of 950 MPa

min. | R900(TM10)

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

1.76e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.76e-05 1/K

average value between 20-300°C

Specific heat capacity

399 J/(kg·K)

Show Supplier Material materials with Specific heat capacity of 399 J/(kg·K)

Thermal conductivity

20 °C

190 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 190 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20 °C

0.0024 S/m

Show Supplier Material materials with Electrical conductivity of 0.0024 S/m

Specific Electrical conductivity

20 °C

42 % IACS

Show Supplier Material materials with Specific Electrical conductivity of 42 % IACS

Chemical properties

PropertyValue

Copper

Balance

Magnesium

0.15 %

Show Supplier Material materials with Magnesium of 0.15 %

Nickel

4 %

Show Supplier Material materials with Nickel of 4 %

Silicon

0.75 %

Show Supplier Material materials with Silicon of 0.75 %

Technological properties

Property
Application areas

Application target:

Signal ConnectorVery suitable
Power ConnectorSuitable
Miniaturized ConnectorVery suitable
Switch / RelayVery suitable
SemiconductorSuitable


Ideal for miniaturized connector ,especially CPU socket ,relay and SIM card connector etc.

Chemical composition

The chemical composition is the nominal composition of the alloy

Coating

Electroplating: Good


Hot dip tinning: Good

Cold Forming

Very good

Machining

Not suitable

Packaging size

Standard coils with outside diameters up to 1200 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons.

Soldering general

Soft soldering: Good

Testings

Fatigue strength:

The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength.


Bending test:

90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack.

Welding

Laser welding: Good


Resistance welding: Average