UNS C52100 boway

Alternative and trade names
boway 52100
Want to keep this datasheet? Save it now in your required format

Description

Excellent formability and high strength combined with low sensitivity against stress corrosion cracking. Very good corrosion resistance as well as excellent solderability. Low hot cracking tendency with resistance welding.

Equivalent Materials

This material data has been provided by Ningbo Boway Alloy Material.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValue

Density

8.8 g/cm³

Show Supplier Material materials with Density of 8.8 g/cm³

Dimension

PropertyValue

Dimensions

Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Electroplated and Hot-dip tinned strip available.

Mechanical

PropertyValueTesting StandardComment

Bendability 180°, bw

0 [-]

Show Supplier Material materials with Bendability 180°, bw of 0 [-]

ASTM B820

R475(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

1 [-]

Show Supplier Material materials with Bendability 180°, bw of 1 [-]

ASTM B820

R550(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

2 [-]

Show Supplier Material materials with Bendability 180°, bw of 2 [-]

ASTM B820

R585(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

4 [-]

Show Supplier Material materials with Bendability 180°, bw of 4 [-]

ASTM B820

R670(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

7 [-]

Show Supplier Material materials with Bendability 180°, bw of 7 [-]

ASTM B820

R725(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

8 [-]

Show Supplier Material materials with Bendability 180°, bw of 8 [-]

ASTM B820

R760(ESH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

Bendability 180°, gw

0 [-]

Show Supplier Material materials with Bendability 180°, gw of 0 [-]

ASTM B820

R475(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

0.5 [-]

Show Supplier Material materials with Bendability 180°, gw of 0.5 [-]

ASTM B820

R550(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

1 [-]

Show Supplier Material materials with Bendability 180°, gw of 1 [-]

ASTM B820

R585(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

2 [-]

Show Supplier Material materials with Bendability 180°, gw of 2 [-]

ASTM B820

R670(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

5 [-]

Show Supplier Material materials with Bendability 180°, gw of 5 [-]

ASTM B820

R725(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

6 [-]

Show Supplier Material materials with Bendability 180°, gw of 6 [-]

ASTM B820

R760(ESH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

Bendability 90°, bw

0 [-]

Show Supplier Material materials with Bendability 90°, bw of 0 [-]

EN ISO 7438

R475(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

0.5 [-]

Show Supplier Material materials with Bendability 90°, bw of 0.5 [-]

EN ISO 7438

R550(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

1 [-]

Show Supplier Material materials with Bendability 90°, bw of 1 [-]

EN ISO 7438

R585(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

2 [-]

Show Supplier Material materials with Bendability 90°, bw of 2 [-]

EN ISO 7438

R670(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

4 [-]

Show Supplier Material materials with Bendability 90°, bw of 4 [-]

EN ISO 7438

R725(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

6 [-]

Show Supplier Material materials with Bendability 90°, bw of 6 [-]

EN ISO 7438

R760(ESH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

Bendability 90°, gw

0 [-]

Show Supplier Material materials with Bendability 90°, gw of 0 [-]

EN ISO 7438

R475(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

0 [-]

Show Supplier Material materials with Bendability 90°, gw of 0 [-]

EN ISO 7438

R550(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

0 [-]

Show Supplier Material materials with Bendability 90°, gw of 0 [-]

EN ISO 7438

R585(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

1.5 [-]

Show Supplier Material materials with Bendability 90°, gw of 1.5 [-]

EN ISO 7438

R670(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

2.5 [-]

Show Supplier Material materials with Bendability 90°, gw of 2.5 [-]

EN ISO 7438

R725(SH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

4 [-]

Show Supplier Material materials with Bendability 90°, gw of 4 [-]

EN ISO 7438

R760(ESH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm

Elastic modulus

115 GPa

Show Supplier Material materials with Elastic modulus of 115 GPa

Elongation

2 %

Show Supplier Material materials with Elongation of 2 %

min. | R760(ESH), A50

3 %

Show Supplier Material materials with Elongation of 3 %

min. | R725(SH), A50

10 %

Show Supplier Material materials with Elongation of 10 %

min. | R670(EH), A50

12 %

Show Supplier Material materials with Elongation of 12 %

min. | R585(H), A50

18 %

Show Supplier Material materials with Elongation of 18 %

min. | R550(3/4H), A50

25 %

Show Supplier Material materials with Elongation of 25 %

min. | R475(1/2H), A50

Hardness, Vickers

150 - 205 [-]

Show Supplier Material materials with Hardness, Vickers of 150 - 205 [-]

R475(1/2H) | For reference only

170 - 210 [-]

Show Supplier Material materials with Hardness, Vickers of 170 - 210 [-]

R550(3/4H) | For reference only

185 - 235 [-]

Show Supplier Material materials with Hardness, Vickers of 185 - 235 [-]

R585(H) | For reference only

210 - 260 [-]

Show Supplier Material materials with Hardness, Vickers of 210 - 260 [-]

R670(EH) | For reference only

230 - 270 [-]

Show Supplier Material materials with Hardness, Vickers of 230 - 270 [-]

R725(SH) | For reference only

245 - 285 [-]

Show Supplier Material materials with Hardness, Vickers of 245 - 285 [-]

R760(ESH) | For reference only

Poisson's ratio

0.33 [-]

Show Supplier Material materials with Poisson's ratio of 0.33 [-]

Tensile strength

475 - 580 MPa

Show Supplier Material materials with Tensile strength of 475 - 580 MPa

R475(1/2H)

550 - 635 MPa

Show Supplier Material materials with Tensile strength of 550 - 635 MPa

R550(3/4H)

585 - 690 MPa

Show Supplier Material materials with Tensile strength of 585 - 690 MPa

R585(H)

670 - 770 MPa

Show Supplier Material materials with Tensile strength of 670 - 770 MPa

R670(EH)

725 - 820 MPa

Show Supplier Material materials with Tensile strength of 725 - 820 MPa

R725(SH)

760 - 840 MPa

Show Supplier Material materials with Tensile strength of 760 - 840 MPa

R760(ESH)

Yield strength

350 MPa

Show Supplier Material materials with Yield strength of 350 MPa

min. | R475(1/2H)

485 MPa

Show Supplier Material materials with Yield strength of 485 MPa

min. | R550(3/4H)

540 MPa

Show Supplier Material materials with Yield strength of 540 MPa

min. | R585(H)

635 MPa

Show Supplier Material materials with Yield strength of 635 MPa

min. | R670(EH)

690 MPa

Show Supplier Material materials with Yield strength of 690 MPa

min. | R725(SH)

725 MPa

Show Supplier Material materials with Yield strength of 725 MPa

min. | R760(ESH)

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

1.82e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.82e-05 1/K

average value between 20-300°C

Specific heat capacity

377 J/(kg·K)

Show Supplier Material materials with Specific heat capacity of 377 J/(kg·K)

Thermal conductivity

20 °C

67 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 67 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20 °C

0.007 S/m

Show Supplier Material materials with Electrical conductivity of 0.007 S/m

Specific Electrical conductivity

20 °C

12 % IACS

Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS

Chemical properties

PropertyValue

Copper

Balance

Tin

8 %

Show Supplier Material materials with Tin of 8 %

Technological properties

Property
Application areas

Application target:

Signal ConnectorVery suitable
Power ConnectorNot suitable
Miniaturized ConnectorVery suitable
Switch / RelaySuitable
SemiconductorNot recommended


Ideal for BTB connector, audio jack and other miniaturized connectors

Chemical composition

The chemical composition is the nominal composition of the alloy

Coating

Electroplating: Very good


Hot dip tinning: Very good

Cold Forming

Very good

Machining

Not suitable

Packaging size

Standard coils with outside diameters up to 1300 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons.

Soldering general

Soft soldering: Good

Testings

Fatigue strength:

The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength.


Bending test:

90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack.

Welding

Laser welding: Good


Resistance welding: Good