General
Property | Value |
---|---|
Density | 8.88 g/cm³ Show Supplier Material materials with Density of 8.88 g/cm³ |
Dimension
Property | Value |
---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Electroplated and HDT strip available. |
Mechanical
Property | Value | Testing Standard | Comment |
---|---|---|---|
Bendability 180°, bw | 1 [-] Show Supplier Material materials with Bendability 180°, bw of 1 [-] | ASTM B820 | R440(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Bendability 180°, bw of 1.5 [-] | ASTM B820 | R520(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2.5 [-] Show Supplier Material materials with Bendability 180°, bw of 2.5 [-] | ASTM B820 | R560(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
5 [-] Show Supplier Material materials with Bendability 180°, bw of 5 [-] | ASTM B820 | R620(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Bendability 180°, gw | 0 [-] Show Supplier Material materials with Bendability 180°, gw of 0 [-] | ASTM B820 | R440(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
0.5 [-] Show Supplier Material materials with Bendability 180°, gw of 0.5 [-] | ASTM B820 | R520(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Bendability 180°, gw of 1.5 [-] | ASTM B820 | R560(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Bendability 180°, gw of 2 [-] | ASTM B820 | R620(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Bendability 90°, bw | 0.5 [-] Show Supplier Material materials with Bendability 90°, bw of 0.5 [-] | EN ISO 7438 | R440(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
0.5 [-] Show Supplier Material materials with Bendability 90°, bw of 0.5 [-] | EN ISO 7438 | R520(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Bendability 90°, bw of 1.5 [-] | EN ISO 7438 | R560(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Bendability 90°, bw of 2 [-] | EN ISO 7438 | R620(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Bendability 90°, gw | 0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | EN ISO 7438 | R440(1/2H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | EN ISO 7438 | R520(3/4H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
0.5 [-] Show Supplier Material materials with Bendability 90°, gw of 0.5 [-] | EN ISO 7438 | R560(H) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1 [-] Show Supplier Material materials with Bendability 90°, gw of 1 [-] | EN ISO 7438 | R620(EH) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Elastic modulus | 120 GPa Show Supplier Material materials with Elastic modulus of 120 GPa | ||
Elongation | 1 % Show Supplier Material materials with Elongation of 1 % | min. | R620(EH), A50 | |
3 % Show Supplier Material materials with Elongation of 3 % | min. | R560(H), A50 | ||
6 % Show Supplier Material materials with Elongation of 6 % | min. | R520(3/4H), A50 | ||
8 % Show Supplier Material materials with Elongation of 8 % | min. | R440(1/2H), A50 | ||
Hardness, Vickers | 140 - 170 [-] Show Supplier Material materials with Hardness, Vickers of 140 - 170 [-] | R440(1/2H) | For reference only | |
150 - 190 [-] Show Supplier Material materials with Hardness, Vickers of 150 - 190 [-] | R520(3/4H) | For reference only | ||
170 - 210 [-] Show Supplier Material materials with Hardness, Vickers of 170 - 210 [-] | R560(H) | For reference only | ||
190 - 220 [-] Show Supplier Material materials with Hardness, Vickers of 190 - 220 [-] | R620(EH) | For reference only | ||
Poisson's ratio | 0.33 [-] Show Supplier Material materials with Poisson's ratio of 0.33 [-] | ||
Tensile strength | 440 - 540 MPa Show Supplier Material materials with Tensile strength of 440 - 540 MPa | R440(1/2H) | |
520 - 620 MPa Show Supplier Material materials with Tensile strength of 520 - 620 MPa | R520(3/4H) | ||
560 - 660 MPa Show Supplier Material materials with Tensile strength of 560 - 660 MPa | R560(H) | ||
620 - 720 MPa Show Supplier Material materials with Tensile strength of 620 - 720 MPa | R620(EH) | ||
Yield strength | 420 MPa Show Supplier Material materials with Yield strength of 420 MPa | min. | R440(1/2H) | |
500 MPa Show Supplier Material materials with Yield strength of 500 MPa | min. | R520(3/4H) | ||
550 MPa Show Supplier Material materials with Yield strength of 550 MPa | min. | R560(H) | ||
590 MPa Show Supplier Material materials with Yield strength of 590 MPa | min. | R620(EH) |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 1.67e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.67e-05 1/K | average value between 20-300°C | |
Specific heat capacity | 430 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 430 J/(kg·K) | ||
Thermal conductivity | 20 °C | 125 W/(m·K) Show Supplier Material materials with Thermal conductivity of 125 W/(m·K) |
Electrical
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | Application target: | |
Chemical composition | The chemical composition is the nominal composition of the alloy | |
Coating | Electroplating: Good Hot dip tinning: Good | |
Cold Forming | Good | |
Machining | Not suitable | |
Packaging size | Standard coils with outside diameters up to 1200 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
Soldering general | Soft soldering: Very good | |
Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
Welding | Laser welding: Good Resistance welding: Good |