Properties
General
| Property | Value |
|---|---|
Density | 8.9 g/cm³ Show Supplier Material materials with Density of 8.9 g/cm³ |
Dimension
| Property | Value |
|---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Electroplated and Hot-dip tinned strip available. |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Bendability 180°, bw | 1 [-] Show Supplier Material materials with Bendability 180°, bw of 1 [-] | ASTM B820 | R400 | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1.5 [-] Show Supplier Material materials with Bendability 180°, bw of 1.5 [-] | ASTM B820 | R490 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Bendability 180°, bw of 2 [-] | ASTM B820 | R520 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Bendability 180°, bw of 2 [-] | ASTM B820 | R580 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Bendability 180°, gw | 0.5 [-] Show Supplier Material materials with Bendability 180°, gw of 0.5 [-] | ASTM B820 | R400 | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Bendability 180°, gw of 1 [-] | ASTM B820 | R490 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Bendability 180°, gw of 1.5 [-] | ASTM B820 | R520 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Bendability 180°, gw of 2 [-] | ASTM B820 | R580 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Bendability 90°, bw | 0.5 [-] Show Supplier Material materials with Bendability 90°, bw of 0.5 [-] | EN ISO 7438 | R400 | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
0.5 [-] Show Supplier Material materials with Bendability 90°, bw of 0.5 [-] | EN ISO 7438 | R490 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
0.5 [-] Show Supplier Material materials with Bendability 90°, bw of 0.5 [-] | EN ISO 7438 | R520 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1 [-] Show Supplier Material materials with Bendability 90°, bw of 1 [-] | EN ISO 7438 | R580 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Bendability 90°, gw | 0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | EN ISO 7438 | R400 | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | EN ISO 7438 | R490 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
0.5 [-] Show Supplier Material materials with Bendability 90°, gw of 0.5 [-] | EN ISO 7438 | R520 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1 [-] Show Supplier Material materials with Bendability 90°, gw of 1 [-] | EN ISO 7438 | R580 | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Elastic modulus | 127 GPa Show Supplier Material materials with Elastic modulus of 127 GPa | ||
Elongation | 8 % Show Supplier Material materials with Elongation of 8 % | min. | R400, A50 | |
8 % Show Supplier Material materials with Elongation of 8 % | min. | R580, A50 | ||
9 % Show Supplier Material materials with Elongation of 9 % | min. | R520, A50 | ||
10 % Show Supplier Material materials with Elongation of 10 % | min. | R490, A50 | ||
Hardness, Vickers | 120 - 150 [-] Show Supplier Material materials with Hardness, Vickers of 120 - 150 [-] | R400 | For reference only | |
140 - 170 [-] Show Supplier Material materials with Hardness, Vickers of 140 - 170 [-] | R490 | For reference only | ||
150 - 180 [-] Show Supplier Material materials with Hardness, Vickers of 150 - 180 [-] | R520 | For reference only | ||
170 - 200 [-] Show Supplier Material materials with Hardness, Vickers of 170 - 200 [-] | R580 | For reference only | ||
Poisson's ratio | 0.33 [-] Show Supplier Material materials with Poisson's ratio of 0.33 [-] | ||
Tensile strength | 400 - 460 MPa Show Supplier Material materials with Tensile strength of 400 - 460 MPa | R400 | |
490 - 550 MPa Show Supplier Material materials with Tensile strength of 490 - 550 MPa | R490 | ||
520 - 590 MPa Show Supplier Material materials with Tensile strength of 520 - 590 MPa | R520 | ||
580 - 650 MPa Show Supplier Material materials with Tensile strength of 580 - 650 MPa | R580 | ||
Yield strength | 360 MPa Show Supplier Material materials with Yield strength of 360 MPa | min. | R400 | |
410 MPa Show Supplier Material materials with Yield strength of 410 MPa | min. | R490 | ||
440 MPa Show Supplier Material materials with Yield strength of 440 MPa | min. | R520 | ||
540 MPa Show Supplier Material materials with Yield strength of 540 MPa | min. | R580 |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 1.68e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.68e-05 1/K | average value between 20-300°C | |
Specific heat capacity | 377 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 377 J/(kg·K) | ||
Thermal conductivity | 20 °C | 250 W/(m·K) Show Supplier Material materials with Thermal conductivity of 250 W/(m·K) |
Electrical
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Application target: | |
| Chemical composition | The chemical composition is the nominal composition of the alloy | |
| Coating | Electroplating: Good Hot dip tinning: Good | |
| Cold Forming | Very good | |
| Machining | Not suitable | |
| Packaging size | Standard coils with outside diameters up to 1200 mm. Traverse-wound coils with drum weights up to 500 kg.Multiple-coil up to 3 tons. | |
| Soldering general | Soft soldering: Good | |
| Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
| Welding | Laser welding: Suitable Resistance welding: Average | |