LNP™ LUBRICOMP™ Compound NX20BSR

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP NX20BSR is a Low gloss black PC/ABS compound with good Buzz, Squeak and Rattle (BSR) performance. Added features include low slip-stick and lubricated

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Coefficient of friction		0.33 [-] Show Supplier Material materials with Coefficient of friction of 0.33 [-]
Coefficient of friction, kinetic		0.33 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.33 [-]	ASTM D 3702 Modified: Manual
Density	23.0 °C	1.12 g/cm³ Show Supplier Material materials with Density of 1.12 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.1 % Show Supplier Material materials with Moisture absorption of 0.1 %	ASTM D 570 \| (23°C/50% RH/24 hrs)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	5 % Show Supplier Material materials with Elongation of 5 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.1 GPa Show Supplier Material materials with Flexural modulus of 2.1 GPa	ISO 178 \| 2 mm/min
Impact strength, Charpy notched	23.0 °C	49 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 49 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	40 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 40 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	463 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 463 J/m	ASTM D 256 \| notched, -30°C
Impact strength, Izod unnotched	23.0 °C	208 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 208 kJ/m²	ISO 180/1U \| unnotched 80104, 23°C
Tensile strength	23.0 °C	50 MPa Show Supplier Material materials with Tensile strength of 50 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	104 - 125 °C Show Supplier Material materials with Heat deflection temperature of 104 - 125 °C
Heat deflection temperature, 0.45 MPa	125 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 125 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	104 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 104 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature	124 °C Show Supplier Material materials with Vicat softening temperature of 124 °C	ISO 306 \| Rate B/120

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		23 g/10min Show Supplier Material materials with Melt mass-flow rate of 23 g/10min	ASTM D 1238 \| 260°C/5.0 kgf
Melt volume-flow rate		21 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 21 cm³/10min	ISO 1133 \| MVR at 260°C/5.0 kg
Shrinkage	23.0 °C	0.7 % Show Supplier Material materials with Shrinkage of 0.7 %	SABIC method
Shrinkage, transverse	23.0 °C	0.8 % Show Supplier Material materials with Shrinkage, transverse of 0.8 %	SABIC method

Technological properties

Property
Application areas	Automotive , Console, Infotainment/Telematic, Interior, Interior trims
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 105 to 110.0°C Maximum Moisture Content: 0.02% Melt Temperature: 270 to 310.0°C Front - Zone 3 Temperature: 260 to 300.0°C Middle - Zone 2 Temperature: 255 to 285.0°C Rear - Zone 1 Temperature: 250 to 290.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Drying Time (Cumulative): 3 to 4.0hrs Drying Time (Cumulative): 9hrs Mold Temperature: 60 to 80.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.