LNP™ THERMOCOMP™ Compound JF006E - Europe

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP JF006E is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.62 g/cm³

Show Supplier Material materials with Density of 1.62 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

1.9 %

Show Supplier Material materials with Elongation of 1.9 %

ISO 527 | break

Flexural modulus

23.0 °C

9.1 GPa

Show Supplier Material materials with Flexural modulus of 9.1 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

209 MPa

Show Supplier Material materials with Flexural strength of 209 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

40 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 40 kJ/m²

ISO 180/1U | unnotched 80*10*4

Tensile strength

23.0 °C

145 MPa

Show Supplier Material materials with Tensile strength of 145 MPa

ISO 527 | break

Thermal

PropertyValueComment

Heat deflection temperature

211 °C

Show Supplier Material materials with Heat deflection temperature of 211 °C

Heat deflection temperature, 1.80 MPa

211 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 211 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

190 °C

Show Supplier Material materials with Relative temperature index, electrical of 190 °C

UL 746B

Relative temperature index, mechanical impact

190 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 190 °C

UL 746B

Relative temperature index, mechanical strength

190 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 190 °C

UL 746B

Flammability

UL Recognized, 94V-0 Flame Class Rating: 0.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283860- -

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Meter Water

Availability

Europe,Americas

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.