General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.6 GPa Show Supplier Material materials with Elastic modulus of 3.6 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ASTM D 638 | yld, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 3.3 GPa Show Supplier Material materials with Flexural modulus of 3.3 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 151 MPa Show Supplier Material materials with Flexural strength of 151 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Impact strength, Izod notched | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m² | ASTM D 256 | notched, 23°C |
Taber Abrasion | 23.0 °C | 10 mg/1000cy Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Tensile strength | 23.0 °C | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | ASTM D 638 | yld, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.58E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.58E-5 1/K | ASTM E 831 | -20°C to 150°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 5.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.4E-5 1/K | ASTM E 831 | -20°C to 150°C |
Heat deflection temperature | 201 - 210 °C Show Supplier Material materials with Heat deflection temperature of 201 - 210 °C | ||
Heat deflection temperature, 0.45 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 210 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 201 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 201 °C | ASTM D 648 | 6.4 mm, unannealed | |
Thermal conductivity | 23.0 °C | 0.22 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K) | ASTM C177 |
Vicat softening temperature | 218 °C Show Supplier Material materials with Vicat softening temperature of 218 °C | ASTM D 1525 | Rate B/50 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 32.7 kV/mm Show Supplier Material materials with Dielectric strength of 32.7 kV/mm | ASTM D 149 | in air, 1.6 mm |
Dissipation factor | 23.0 °C | 2.5E-3 [-] Show Supplier Material materials with Dissipation factor of 2.5E-3 [-] | ASTM D 150 | 2450 MHz |
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Application areas | Air Cabin Interiors, Composite, Wireless Communications | |
Availability | Asia,Americas | |
Processing methods | Melt Temperature: 350 to 400.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |