General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.57 g/cm³ Show Supplier Material materials with Density of 1.57 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.57 [-] Show Supplier Material materials with Relative density of 1.57 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.4 GPa Show Supplier Material materials with Elastic modulus of 10.4 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.4 % Show Supplier Material materials with Elongation of 2.4 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 8.9 GPa Show Supplier Material materials with Flexural modulus of 8.9 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 184 MPa Show Supplier Material materials with Flexural strength of 184 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 6.9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6.9 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 55 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 55 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 43 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 43 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 585 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 585 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 131 MPa Show Supplier Material materials with Tensile strength of 131 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.1E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature | 205 - 222 °C Show Supplier Material materials with Heat deflection temperature of 205 - 222 °C | ||
Heat deflection temperature, 0.45 MPa | 222 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 222 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 205 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 214 °C Show Supplier Material materials with Vicat softening temperature of 214 °C | ISO 306 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 12 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | MVR at 265°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.21 % Show Supplier Material materials with Shrinkage of 0.21 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 1.21 % Show Supplier Material materials with Shrinkage, transverse of 1.21 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Food Container | |
Availability | Europe | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |