General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.48 g/cm³ Show Supplier Material materials with Density of 1.48 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12.3 GPa Show Supplier Material materials with Elastic modulus of 12.3 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.5 % Show Supplier Material materials with Elongation of 1.5 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 11 GPa Show Supplier Material materials with Flexural modulus of 11 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 217 MPa Show Supplier Material materials with Flexural strength of 217 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 1 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 1 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 160 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 160 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 833 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 833 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 113 MPa Show Supplier Material materials with Tensile strength of 113 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Value | Comment |
---|---|---|
Heat deflection temperature | 166 - 176 °C Show Supplier Material materials with Heat deflection temperature of 166 - 176 °C | |
Heat deflection temperature, 0.45 MPa | 176 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 176 °C | ASTM D 648 | 3.2 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 166 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 166 °C | ASTM D 648 | 3.2mm, unannealed |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Battery Cell, Electronic Components, Personal Computing | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |