General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Elastic modulus of 2.6 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 50 % Show Supplier Material materials with Elongation of 50 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 90 MPa Show Supplier Material materials with Flexural strength of 90 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 650 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 650 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 130 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 130 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2150 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2150 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 40 MPa Show Supplier Material materials with Tensile strength of 40 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.4E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 105 - 117 °C Show Supplier Material materials with Heat deflection temperature of 105 - 117 °C | ||||
Heat deflection temperature, 0.45 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 117 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 105 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 105 °C | ASTM D 648 | 3.2mm, unannealed | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103685620- - <br> UL Recognized, 94V-0 Flame Class Rating: 0.8mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 2.8 [-] Show Supplier Material materials with Dielectric constant of 2.8 [-] | SABIC method | 20 GHz |
Dielectric constant, 10GHz | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 2.9 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 2.9 [-] | SABIC method |
Dissipation factor | 23.0 °C | 6E-3 [-] Show Supplier Material materials with Dissipation factor of 6E-3 [-] | SABIC method |
Dissipation factor, 1GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 7E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 7E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 16 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 16 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | ASTM D 955 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |