Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 6 % Show Supplier Material materials with Elongation of 6 % | SABIC - Japan Method | break |
Flexural modulus | 23.0 °C | 6.4 GPa Show Supplier Material materials with Flexural modulus of 6.4 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 113 MPa Show Supplier Material materials with Flexural strength of 113 MPa | ASTM D 790 |
Tensile strength | 23.0 °C | 75 MPa Show Supplier Material materials with Tensile strength of 75 MPa | SABIC - Japan Method | yield |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.4E-5 - 3.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.4E-5 - 3.5E-5 1/K | TMA | -30°C to 30°C |
Heat deflection temperature | 116 °C Show Supplier Material materials with Heat deflection temperature of 116 °C | ||
Heat deflection temperature, 1.80 MPa | 116 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 116 °C | ASTM D 648 | 6.4 mm, unannealed |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 19.2 g/10min Show Supplier Material materials with Melt mass-flow rate of 19.2 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Shrinkage | 23.0 °C | 2.5 % Show Supplier Material materials with Shrinkage of 2.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Photo/Video Camera, Personal Computing, Electronic Components, Enclosure/Housing/Cover, Document Handling, Data Transfer, ATM/Ticket Machine | |
Availability | Asia | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |