Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.51 - 0.57 [-] Show Supplier Material materials with Coefficient of friction of 0.51 - 0.57 [-] | ||
Coefficient of friction, kinetic | 0.51 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.51 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.57 [-] Show Supplier Material materials with Coefficient of friction, static of 0.57 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.58 g/cm³ Show Supplier Material materials with Density of 1.58 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.58 [-] Show Supplier Material materials with Relative density of 1.58 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 0.3 % Show Supplier Material materials with Water absorption of 0.3 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 11.5 GPa Show Supplier Material materials with Elastic modulus of 11.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.3 % Show Supplier Material materials with Elongation of 2.3 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 10.1 GPa Show Supplier Material materials with Flexural modulus of 10.1 GPa | ISO 178 | 2 mm/min |
Flexural strain | 23.0 °C | 4.8 % Show Supplier Material materials with Flexural strain of 4.8 % | ISO 178 | break, 2 mm/min, 180°C |
Flexural strength | 23.0 °C | 260 MPa Show Supplier Material materials with Flexural strength of 260 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U | unnotched 80*10*4, -40°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 730 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 730 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 8 J Show Supplier Material materials with Instrumented Impact, Total Energy of 8 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 188 MPa Show Supplier Material materials with Tensile strength of 188 MPa | ISO 527 | break, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.2E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 5.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.8E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature | 275 - 293 °C Show Supplier Material materials with Heat deflection temperature of 275 - 293 °C | ||
Heat deflection temperature, 0.45 MPa | 293 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 293 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 275 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 275 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Specific heat capacity | 23.0 °C | 1722 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1722 J/(kg·K) | ASTM E 1269 |
Thermal conductivity | 23.0 °C | 0.24 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.24 W/(m·K) | ASTM D 5930 |
Vicat softening temperature | 258 °C Show Supplier Material materials with Vicat softening temperature of 258 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 28 g/10min Show Supplier Material materials with Melt mass-flow rate of 28 g/10min | ASTM D 1238 | 340°C/1.2 kgf | |
Melt volume-flow rate | 24 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 24 cm³/10min | ISO 1133 | MVR at 340°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.8 % Show Supplier Material materials with Shrinkage, transverse of 0.8 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Sensor, Laundry Dryer, Medical Device, Exhaust System, Forward Lighting, Engine Component, Electrical, EV Infrastructure, Gear/Bearing/Slider, Heavy Vehicles, Lawn/Garden, Electronic Components, Amusement Machine, Auto Aftermarket, Circuit Protection, Air Intake System, Building Element | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120 to 150.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |