Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.9 GPa Show Supplier Material materials with Elastic modulus of 1.9 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 4 % Show Supplier Material materials with Elongation of 4 % | ISO 527 | yield, 50 mm/min |
Flexural modulus | 23.0 °C | 2 GPa Show Supplier Material materials with Flexural modulus of 2 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 68 MPa Show Supplier Material materials with Flexural strength of 68 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 645 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 645 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 645 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 645 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 34 J Show Supplier Material materials with Instrumented Impact, at Peak of 34 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 42 MPa Show Supplier Material materials with Tensile strength of 42 MPa | ISO 527 | yield, 50 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 64 - 123 °C Show Supplier Material materials with Heat deflection temperature of 64 - 123 °C | ||
Heat deflection temperature, 0.45 MPa | 123 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 123 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 64 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 64 °C | ASTM D 648 | 3.2mm, unannealed | |
Vicat softening temperature | 136 °C Show Supplier Material materials with Vicat softening temperature of 136 °C | ASTM D 1525 | Rate B/120 | |
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104427473 - - <br> UL Recognized, 94HB Flame Class Rating: ≥0.75mm UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 11 g/10min Show Supplier Material materials with Melt mass-flow rate of 11 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Melt volume-flow rate | 10 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min | ASTM D 1238 | MVR at 250°C/5 kg | |
Shrinkage | 23.0 °C | 1.2 % Show Supplier Material materials with Shrinkage of 1.2 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 1.2 % Show Supplier Material materials with Shrinkage, transverse of 1.2 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Healthcare | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |