General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.32 g/cm³ Show Supplier Material materials with Density of 1.32 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.01 % Show Supplier Material materials with Moisture absorption of 0.01 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.33 [-] Show Supplier Material materials with Relative density of 1.33 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Water absorption of 0.06 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.3 GPa Show Supplier Material materials with Elastic modulus of 8.3 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Supplier Material materials with Elongation of 2 % | ISO 527 | yield, 5 mm/min |
Flexural modulus | 23.0 °C | 8 GPa Show Supplier Material materials with Flexural modulus of 8 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 168 MPa Show Supplier Material materials with Flexural strength of 168 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 98 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 98 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 27 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 27 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 449 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 449 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 105 MPa Show Supplier Material materials with Tensile strength of 105 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.68E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.68E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.67E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.67E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 130 - 135 °C Show Supplier Material materials with Heat deflection temperature of 130 - 135 °C | ||||
Heat deflection temperature, 0.45 MPa | 135 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 130 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 130 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Vicat softening temperature | 129 °C Show Supplier Material materials with Vicat softening temperature of 129 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104050517- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.75mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 200 V Show Supplier Material materials with Comparative tracking index of 200 V | IEC 60112 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 56 g/10min Show Supplier Material materials with Melt mass-flow rate of 56 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Melt volume-flow rate | 47 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 47 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.34 % Show Supplier Material materials with Shrinkage of 0.34 % | ISO 294 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.53 % Show Supplier Material materials with Shrinkage, transverse of 0.53 % | ISO 294 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 2hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |