NORYL™ Resin EX130 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ EX130 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection molding grade exhibits a good balance of impact resistance and surface aesthetics. NORYL EX130 resin, with its low warpage and dimensional stability, is an excellent candidate for automotive exterior applications.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Automotive

General Automotive Parts

Automotive Exterior

Construction

Lighting

Aerospace

Consumer Goods

Decorative Applications

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.06 [-] Show Supplier Material materials with Relative density of 1.06 [-]	ASTM D 792
Water absorption	23.0 °C	0.06 % Show Supplier Material materials with Water absorption of 0.06 %	ASTM D 570 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	50 % Show Supplier Material materials with Elongation of 50 %	SABIC - Japan Method \| break
Flexural modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa	ASTM D 790
Flexural strength	23.0 °C	78 MPa Show Supplier Material materials with Flexural strength of 78 MPa	ASTM D 790
Impact strength, Izod notched	23.0 °C	235 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 235 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	235 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 235 J/m	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	53 MPa Show Supplier Material materials with Tensile strength of 53 MPa	SABIC - Japan Method \| yield

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	5.5E-5 - 7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.5E-5 - 7.5E-5 1/K	TMA \| -30°C to 30°C
Heat deflection temperature		127 °C Show Supplier Material materials with Heat deflection temperature of 127 °C
Heat deflection temperature, 1.80 MPa		127 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 127 °C	ASTM D 648 \| 6.4 mm, unannealed

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		4.6 g/10min Show Supplier Material materials with Melt mass-flow rate of 4.6 g/10min	ASTM D 1238 \| 250°C/10.0 kgf
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Air Cabin Interiors, Auto Aftermarket, Wheel Cover, Seating/Chair, Non-LED Lighting
Availability	Asia
Processing methods	Drying Temperature: 80 to 90.0°C Drying Time: 2 to 4.0hrs Melt Temperature: 275 to 310.0°C Nozzle Temperature: 270 to 305.0°C Front - Zone 3 Temperature: 270 to 310.0°C Middle - Zone 2 Temperature: 265 to 300.0°C Rear - Zone 1 Temperature: 245 to 290.0°C Mold Temperature: 70 to 110.0°C Screw Speed: 40 to 60.0rpm Back Pressure: 0.5 to 1.4MPa
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.