Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.26 [-] Show Supplier Material materials with Relative density of 1.26 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 6.6 % Show Supplier Material materials with Elongation of 6.6 % | SABIC - Japan Method | brk, Type I, 10 mm/min |
Flexural modulus | 23.0 °C | 9.7 GPa Show Supplier Material materials with Flexural modulus of 9.7 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 155 MPa Show Supplier Material materials with Flexural strength of 155 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Impact strength, Izod notched | 23.0 °C | 66.4 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 66.4 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 66.4 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 66.4 J/m | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 120.7 MPa Show Supplier Material materials with Tensile strength of 120.7 MPa | SABIC - Japan Method | yld, Type I, 10 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ash content | 23.0 °C | 17.82 % Show Supplier Material materials with Ash content of 17.82 % | w/w | ||
Heat deflection temperature | 133.4 °C Show Supplier Material materials with Heat deflection temperature of 133.4 °C | ||||
Heat deflection temperature, 1.80 MPa | 133.4 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 133.4 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=237042- - <br> UL Recognized, 94V-1 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥3mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 42000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 42000 Ω | ASTM D 257 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 10.6 g/10min Show Supplier Material materials with Melt mass-flow rate of 10.6 g/10min | ASTM D 1238 | 300°C/5.0 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Electrical Components & Infrastructure | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |