Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.01 g/cm³ Show Supplier Material materials with Density of 1.01 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.1 % Show Supplier Material materials with Moisture absorption of 1.1 % | ISO 62 | (23°C / 50% RH) |
Water absorption | 23.0 °C | 0.7 % Show Supplier Material materials with Water absorption of 0.7 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.4 GPa Show Supplier Material materials with Elastic modulus of 0.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 50 % Show Supplier Material materials with Elongation of 50 % | ≥, ISO 527 | break, 50 mm/min | ||
Hardness, Shore D | 23.0 °C | 61 [-] Show Supplier Material materials with Hardness, Shore D of 61 [-] | ISO 868 | ||
Impact strength, Charpy notched | 23.0 °C | 120 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 120 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm | ||
Tensile strength | 23.0 °C | 22 MPa Show Supplier Material materials with Tensile strength of 22 MPa | ISO 527 | yield, 50 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Thermal
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Melt Temperature: 260°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |