NORYL GTX™ Resin GTX820 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 820 resin is a 20% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 4000 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX GTX830 resin is an excellent candidate for a wide variety of applications including valves for water management.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Exterior

Construction

Water Management

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.245 g/cm³ Show Supplier Material materials with Density of 1.245 g/cm³	ASTM D 792
Moisture absorption	23.0 °C	1 % Show Supplier Material materials with Moisture absorption of 1 %	ASTM D 570 \| (23°C/50% RH/24 hrs)
Water absorption	23.0 °C	0.5 % Show Supplier Material materials with Water absorption of 0.5 %	ASTM D 570 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	7 % Show Supplier Material materials with Elongation of 7 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	6 GPa Show Supplier Material materials with Flexural modulus of 6 GPa	ASTM D 790 \| 2.6 mm/min, 100 mm span
Flexural strength	23.0 °C	194 MPa Show Supplier Material materials with Flexural strength of 194 MPa	ASTM D 790 \| yld, 2.6 mm/min, 100 mm span
Tensile strength	23.0 °C	117 MPa Show Supplier Material materials with Tensile strength of 117 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3.06E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.06E-5 1/K	ASTM E 831 \| -20°C to 150°C
Vicat softening temperature		248 °C Show Supplier Material materials with Vicat softening temperature of 248 °C	ASTM D 1525 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.3 % Show Supplier Material materials with Shrinkage of 0.3 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Pump, Heavy Vehicles, Electronic Components, Auto Aftermarket
Availability	Asia,Americas
Processing methods	Vent Depth: 0.013 to 0.038mm Drying Time: 3 to 4.0hrs Mold Temperature: 75 to 120.0°C Melt Temperature: 280 to 305.0°C Drying Temperature: 95 to 105.0°C Maximum Moisture Content: 0.07% Screw Speed: 20 to 100.0rpm Drying Time (Cumulative): 8hrs Minimum Moisture Content: 0.02% Rear - Zone 1 Temperature: 265 to 305.0°C Nozzle Temperature: 280 to 305.0°C Back Pressure: 0.3 to 1.4MPa Shot to Cylinder Size: 30 to 50.0% Front - Zone 3 Temperature: 275 to 305.0°C Middle - Zone 2 Temperature: 270 to 305.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.