NORYL GTX™ Resin GTX820 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 820 resin is a 20% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 4000 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX GTX830 resin is an excellent candidate for a wide variety of applications including valves for water management.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Exterior

Construction

Water Management

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.25 g/cm³ Show Supplier Material materials with Density of 1.25 g/cm³	ISO 1183
Moisture absorption	23.0 °C	1.08 % Show Supplier Material materials with Moisture absorption of 1.08 %	ISO 62 \| (23°C / 50% RH)
Water absorption	23.0 °C	3.2 % Show Supplier Material materials with Water absorption of 3.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	2.5 % Show Supplier Material materials with Elongation of 2.5 %	ISO 527 \| yield, 5 mm/min
Flexural modulus	23.0 °C	5.2 GPa Show Supplier Material materials with Flexural modulus of 5.2 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	217 MPa Show Supplier Material materials with Flexural strength of 217 MPa	ISO 178 \| break, 2 mm/min
Tensile strength	23.0 °C	95 MPa Show Supplier Material materials with Tensile strength of 95 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Vicat softening temperature		252 °C Show Supplier Material materials with Vicat softening temperature of 252 °C	ISO 306 \| Rate A/50

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Pump, Heavy Vehicles, Electronic Components, Auto Aftermarket
Availability	Asia,Americas
Processing methods	Drying Temperature: 100 to 110.0°C Mold Temperature: 80 to 100.0°C Nozzle Temperature: 270 to 290.0°C Middle - Zone 2 Temperature: 270 to 290.0°C Rear - Zone 1 Temperature: 260 to 280.0°C Hopper Temperature: 60 to 80.0°C Maximum Moisture Content: 0.07% Melt Temperature: 280 to 300.0°C Front - Zone 3 Temperature: 280 to 300.0°C Drying Time: 2 to 3.0hrs
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.