General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.22 % Show Supplier Material materials with Moisture absorption of 0.22 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.2 GPa Show Supplier Material materials with Elastic modulus of 3.2 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 7.6 % Show Supplier Material materials with Elongation of 7.6 % | ISO 527 | break |
Flexural modulus | 23.0 °C | 3.4 GPa Show Supplier Material materials with Flexural modulus of 3.4 GPa | ISO 178 |
Flexural strength | 23.0 °C | 143 MPa Show Supplier Material materials with Flexural strength of 143 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 4 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 26 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 26 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 32 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 32 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 469 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 469 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 4 J Show Supplier Material materials with Instrumented Impact, at Peak of 4 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 86 MPa Show Supplier Material materials with Tensile strength of 86 MPa | ISO 527 | yield |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 184 °C Show Supplier Material materials with Heat deflection temperature of 184 °C | ||
Heat deflection temperature, 1.80 MPa | 184 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 184 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101345280- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101345235- - <br> UL Recognized, 94V-0 Flame Class Rating: 0.35mm UL 94 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 4 to 6.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |