General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.39 - 0.42 [-] Show Supplier Material materials with Coefficient of friction of 0.39 - 0.42 [-] | ||
Coefficient of friction, kinetic | 0.39 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.39 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.42 [-] Show Supplier Material materials with Coefficient of friction, static of 0.42 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.39 g/cm³ Show Supplier Material materials with Density of 1.39 g/cm³ | ASTM D 792 |
Relative density | 23.0 °C | 1.39 [-] Show Supplier Material materials with Relative density of 1.39 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 30.4 GPa Show Supplier Material materials with Elastic modulus of 30.4 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1 % Show Supplier Material materials with Elongation of 1 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 26.3 GPa Show Supplier Material materials with Flexural modulus of 26.3 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 324 MPa Show Supplier Material materials with Flexural strength of 324 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 69 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 69 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 413 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 413 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 11 J Show Supplier Material materials with Instrumented Impact, Total Energy of 11 J | ASTM D 3763 | 23°C |
Poisson's ratio | 23.0 °C | 0.4 [-] Show Supplier Material materials with Poisson's ratio of 0.4 [-] | ASTM E 132 |
Tensile strength | 23.0 °C | 226 MPa Show Supplier Material materials with Tensile strength of 226 MPa | ISO 527 | break, 5 mm/min |
Thermal
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 - 10000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 10000 Ω | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Aircraft Seating | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 4 to 6.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |