LNP™ COLORCOMP™ Compound EX12304C

Want to keep this datasheet? Save it now in your required format

Description

LNP COLORCOMP EX12304C is an unfilled polyetherimide clean compound with extremely high level of cleanliness for the most demanding application. This compound is manufactured using LNP CCS technology.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.27 g/cm³ Show Supplier Material materials with Density of 1.27 g/cm³	ISO 1183
Relative density	23.0 °C	1.27 [-] Show Supplier Material materials with Relative density of 1.27 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	3.2 GPa Show Supplier Material materials with Elastic modulus of 3.2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	6 % Show Supplier Material materials with Elongation of 6 %	ISO 527 \| yield, 5 mm/min
Flexural modulus	23.0 °C	3.3 GPa Show Supplier Material materials with Flexural modulus of 3.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	160 MPa Show Supplier Material materials with Flexural strength of 160 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	32 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 32 J/m	ASTM D 256
Impact strength, Izod unnotched, ASTM	23.0 °C	1335 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1335 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	85 MPa Show Supplier Material materials with Tensile strength of 85 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	5.58E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.58E-5 1/K	ASTM E 831 \| -20°C to 150°C
Heat deflection temperature		193 °C Show Supplier Material materials with Heat deflection temperature of 193 °C
Heat deflection temperature, 1.80 MPa		193 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 193 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Relative temperature index, electrical		105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C	UL 746B
Relative temperature index, mechanical impact		105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C	UL 746B
Relative temperature index, mechanical strength		105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C	UL 746B
Vicat softening temperature		212 °C Show Supplier Material materials with Vicat softening temperature of 212 °C	ISO 306 \| Rate B/120
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102010009- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥3mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	17.8 g/10min Show Supplier Material materials with Melt mass-flow rate of 17.8 g/10min	ASTM D 1238 \| 337°C/6.6 kgf
Melt volume-flow rate	25 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 25 cm³/10min	ISO 1133 \| MVR at 220°C/5.0 kg

Technological properties

Property
Application areas	Data Management
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 150°C Drying Time: 4 to 6.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 360 to 400.0°C Nozzle Temperature: 390 to 400.0°C Front - Zone 3 Temperature: 380 to 400.0°C Middle - Zone 2 Temperature: 370 to 390.0°C Rear - Zone 1 Temperature: 360 to 380.0°C Mold Temperature: 140 to 180.0°C Back Pressure: 0.3 to 0.7MPa Vent Depth: 0.025 to 0.076mm Screw speed (Circumferential speed): 0.2 to 0.3m/s
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.