LNP™ LUBRICOMP™ Compound EX10405H

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP EX10405H is a compound based on Polyetherimide containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Medical Equipment

Surgical Instruments

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Coefficient of friction		0.38 - 0.44 [-] Show Supplier Material materials with Coefficient of friction of 0.38 - 0.44 [-]
Coefficient of friction, kinetic		0.38 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.38 [-]	ASTM D 3702 Modified: Manual
Coefficient of friction, static		0.44 [-] Show Supplier Material materials with Coefficient of friction, static of 0.44 [-]	ASTM D 3702 Modified: Manual
Relative density	23.0 °C	1.4 [-] Show Supplier Material materials with Relative density of 1.4 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	21.5 GPa Show Supplier Material materials with Elastic modulus of 21.5 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	1.3 % Show Supplier Material materials with Elongation of 1.3 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	17.3 GPa Show Supplier Material materials with Flexural modulus of 17.3 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	283 MPa Show Supplier Material materials with Flexural strength of 283 MPa	ASTM D 790 \| brk, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	56 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 56 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	56 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 56 J/m	ASTM D 256
Impact strength, Izod unnotched, ASTM	23.0 °C	476 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 476 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	216 MPa Show Supplier Material materials with Tensile strength of 216 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	213 °C Show Supplier Material materials with Heat deflection temperature of 213 °C
Heat deflection temperature, 1.80 MPa	213 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 213 °C	ASTM D 648 \| 3.2mm, unannealed

Technological properties

Property
Application areas	Medical Device, Surgical Devices
Availability	Europe,Asia,Americas
Processing methods	Drying Time: 4 to 6.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 360 to 400.0°C Front - Zone 3 Temperature: 380 to 400.0°C Middle - Zone 2 Temperature: 370 to 390.0°C Rear - Zone 1 Temperature: 360 to 380.0°C Mold Temperature: 140 to 180.0°C Back Pressure: 0.3 to 0.7MPa Drying Temperature: 150°C Nozzle Temperature: 390 to 400.0°C Screw speed (Circumferential speed): 0.2 to 0.3m/s Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.