LNP™ STAT-KON™ Compound EX03319C

Want to keep this datasheet? Save it now in your required format

Description

LNP STAT-KON EX03319C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding application. A unique feature of this material is its low non-volatile residue (NVR). This compound is manufactured using LNP CCS Technology.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Consumer Goods

General Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.351 g/cm³ Show Supplier Material materials with Density of 1.351 g/cm³	ASTM D 792
Moisture absorption	23.0 °C	0.2 % Show Supplier Material materials with Moisture absorption of 0.2 %	ASTM D 570 \| (23°C/50% RH/24 hrs)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	17 GPa Show Supplier Material materials with Elastic modulus of 17 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	2.3 % Show Supplier Material materials with Elongation of 2.3 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	11.6 GPa Show Supplier Material materials with Flexural modulus of 11.6 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	233 MPa Show Supplier Material materials with Flexural strength of 233 MPa	ASTM D 790 \| brk, 1.3 mm/min, 50 mm span
Impact strength, Charpy notched	23.0 °C	4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	48 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 48 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	48 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 48 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	354 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 354 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	224 MPa Show Supplier Material materials with Tensile strength of 224 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	205 °C Show Supplier Material materials with Heat deflection temperature of 205 °C
Heat deflection temperature, 1.80 MPa	205 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C	ASTM D 648 \| 3.2mm, unannealed

Electrical

Property	Temperature	Value	Comment
Sheet resistivity, ROA	23.0 °C	5000 - 500000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 5000 - 500000 Ω	ASTM D 257
Volume resistivity	23.0 °C	5.00E+3 - 5.00E+6 Ω·cm Show Supplier Material materials with Volume resistivity of 5.00E+3 - 5.00E+6 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.05 % Show Supplier Material materials with Shrinkage of 0.05 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.3 % Show Supplier Material materials with Shrinkage, transverse of 0.3 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Commercial Appliance
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 150°C Drying Time: 4 to 6.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 360 to 400.0°C Nozzle Temperature: 390 to 400.0°C Front - Zone 3 Temperature: 380 to 400.0°C Middle - Zone 2 Temperature: 370 to 390.0°C Rear - Zone 1 Temperature: 360 to 380.0°C Mold Temperature: 140 to 180.0°C Back Pressure: 0.3 to 0.7MPa Vent Depth: 0.025 to 0.076mm Screw speed (Circumferential speed): 0.2 to 0.3m/s
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.