NORYL GTX™ Resin GTX951A

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX951A resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, high melt flow, and added mold release. NORYL GTX951W resin was designed for automotive under-the-hood applications such as power distribution boxes, relay boxes, and junction boxes.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Exterior

Commercial Vehicles

Other Commercial Vehicles

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Moisture absorption	23.0 °C	0.39 % Show Supplier Material materials with Moisture absorption of 0.39 %	ISO 62-4 \| (23°C/50% RH/Equilibrium)
Relative density	23.0 °C	1.1 [-] Show Supplier Material materials with Relative density of 1.1 [-]	ASTM D 792
Water absorption	23.0 °C	1.99 % Show Supplier Material materials with Water absorption of 1.99 %	ISO 62-1 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	51 % Show Supplier Material materials with Elongation of 51 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	98 MPa Show Supplier Material materials with Flexural strength of 98 MPa	ISO 178 \| break, 2 mm/min
Impact strength, Charpy notched	23.0 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²	ISO 179/2C \| -20°C
Impact strength, Izod notched	23.0 °C	8 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m²	ISO 180/4A \| notched 63.512.73.2, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	100 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 100 J/m	ASTM D 256
Instrumented Impact, at Peak	23.0 °C	48 J Show Supplier Material materials with Instrumented Impact, at Peak of 48 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	66 MPa Show Supplier Material materials with Tensile strength of 66 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	1.53E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.53E-4 1/K	ASTM E 831 \| 60°C to 138°C
Heat deflection temperature		181 °C Show Supplier Material materials with Heat deflection temperature of 181 °C
Heat deflection temperature, 0.45 MPa		181 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 181 °C	ISO 75/Be \| Edgew 120104 sp=100mm

Electrical

Property	Temperature	Value	Comment
Dielectric strength	23.0 °C	22.4 kV/mm Show Supplier Material materials with Dielectric strength of 22.4 kV/mm	ASTM D 149 \| in oil, 1.6 mm
Dissipation factor, 1MHz	23.0 °C	0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-]	ASTM D 150

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		24 g/10min Show Supplier Material materials with Melt mass-flow rate of 24 g/10min	ASTM D 1238 \| 280°C/2.16 kgf
Shrinkage	23.0 °C	1.4 % Show Supplier Material materials with Shrinkage of 1.4 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	1.2 % Show Supplier Material materials with Shrinkage, transverse of 1.2 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Auto Electrical, Circuit Protection, Auto Aftermarket, Electronic Components, Recreational Vehicle
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 95 to 105.0°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 8hrs Maximum Moisture Content: 0.07% Minimum Moisture Content: 0.02% Melt Temperature: 270 to 295.0°C Nozzle Temperature: 270 to 295.0°C Front - Zone 3 Temperature: 265 to 295.0°C Middle - Zone 2 Temperature: 260 to 295.0°C Rear - Zone 1 Temperature: 255 to 295.0°C Mold Temperature: 65 to 95.0°C Back Pressure: 0.3 to 1.4MPa Screw Speed: 20 to 100.0rpm Shot to Cylinder Size: 30 to 50.0% Vent Depth: 0.013 to 0.038mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.