General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.52 g/cm³ Show Supplier Material materials with Density of 1.52 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.3 GPa Show Supplier Material materials with Elastic modulus of 10.3 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 2.3 % Show Supplier Material materials with Elongation of 2.3 % | ASTM D 638 | break |
Flexural modulus | 23.0 °C | 10.3 GPa Show Supplier Material materials with Flexural modulus of 10.3 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 262 MPa Show Supplier Material materials with Flexural strength of 262 MPa | ASTM D 790 |
Impact strength, Izod notched | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 85 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 640 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 640 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 166 MPa Show Supplier Material materials with Tensile strength of 166 MPa | ASTM D 638 | break |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 204 °C Show Supplier Material materials with Heat deflection temperature of 204 °C | ||
Heat deflection temperature, 1.80 MPa | 204 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 204 °C | ASTM D 648 | 3.2mm, unannealed | |
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101357467- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 4 to 6.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |