LNP™ THERMOCOMP™ Compound EF004XXP

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP EF004XXP is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: High modulus, high strength, good dimension stability and good warpage control.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.42 g/cm³ Show Supplier Material materials with Density of 1.42 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	7 GPa Show Supplier Material materials with Elastic modulus of 7 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	3.5 % Show Supplier Material materials with Elongation of 3.5 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	7 GPa Show Supplier Material materials with Flexural modulus of 7 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	240 MPa Show Supplier Material materials with Flexural strength of 240 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	60 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 60 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	60 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	150 MPa Show Supplier Material materials with Tensile strength of 150 MPa	ASTM D 638 \| yld, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	210 °C Show Supplier Material materials with Heat deflection temperature of 210 °C
Heat deflection temperature, 1.80 MPa	210 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical	105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C	UL 746B
Relative temperature index, mechanical impact	105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C	UL 746B
Relative temperature index, mechanical strength	105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103690242- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	9.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 9.5 g/10min	ASTM D 1238 \| 337°C/6.7 kgf

Technological properties

Property
Application areas	Wireless Communications
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 150°C Drying Time: 4 to 6.0hrs Melt Temperature: 360 to 400.0°C Nozzle Temperature: 390 to 400.0°C Front - Zone 3 Temperature: 380 to 400.0°C Middle - Zone 2 Temperature: 370 to 390.0°C Rear - Zone 1 Temperature: 360 to 380.0°C Mold Temperature: 140 to 180.0°C Back Pressure: 0.3 to 0.7MPa Screw speed (Circumferential speed): 0.2 to 0.3m/s Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.