General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 244 MPa Show Supplier Material materials with Compressive strength of 244 MPa | SABIC method |
Elastic modulus | 23.0 °C | 27.6 GPa Show Supplier Material materials with Elastic modulus of 27.6 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.2 % Show Supplier Material materials with Elongation of 1.2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 23.1 GPa Show Supplier Material materials with Flexural modulus of 23.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 334 MPa Show Supplier Material materials with Flexural strength of 334 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 81 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 81 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 81 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 81 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 581 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 581 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 12 J Show Supplier Material materials with Instrumented Impact, Total Energy of 12 J | ASTM D 3763 | 23°C |
Poisson's ratio | 23.0 °C | 0.4 [-] Show Supplier Material materials with Poisson's ratio of 0.4 [-] | ASTM E 132 |
Shear modulus | 23.0 °C | 4.7 GPa Show Supplier Material materials with Shear modulus of 4.7 GPa | ASTM D732 |
Shear strength | 23.0 °C | 128 MPa Show Supplier Material materials with Shear strength of 128 MPa | ASTM D732 |
Tensile strength | 23.0 °C | 248 MPa Show Supplier Material materials with Tensile strength of 248 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.2E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.2E-6 1/K | ASTM E 831 | -40°C to 150°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 5.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.8E-5 1/K | ASTM E 831 | -40°C to 150°C |
Heat deflection temperature | 195 °C Show Supplier Material materials with Heat deflection temperature of 195 °C | ||
Heat deflection temperature, 1.80 MPa | 195 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 195 °C | ASTM D 648 | 3.2mm, unannealed |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 22 g/10min Show Supplier Material materials with Melt mass-flow rate of 22 g/10min | ASTM D 1238 | 380°C/6.7 kgf | |
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | ASTM D 955 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage, transverse of 0.1 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Aerospace, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Maximum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |