LNP™ THERMOCOMP™ AM, grade name 6C004XXAR1, is a compound based on PC/PBT resin containing 20% carbon fiber for Large Format Additive manufacturing (LFAM) applications needing improved chemical resistance, lower warp and good surface finish.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Manufacturing

Additive Manufacturing

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.28 [-] Show Supplier Material materials with Relative density of 1.28 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	1.6 % Show Supplier Material materials with Elongation of 1.6 %	Modified ASTM D638 \| 5mm/min
Flexural strength	23.0 °C	149 MPa Show Supplier Material materials with Flexural strength of 149 MPa	Modified ASTM D790 \| 5mm/min
Tensile strength	23.0 °C	27 MPa Show Supplier Material materials with Tensile strength of 27 MPa	Modified ASTM D638 \| 5mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	90 °C Show Supplier Material materials with Heat deflection temperature of 90 °C
Heat deflection temperature, 1.80 MPa	90 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 90 °C	ASTM D 648 \| 3.2mm, annealed,

Technological properties

Property
Application areas	PANELS FOR AUTOMOBILES
Availability	Europe,Asia,Americas
Processing methods	Extruder L/D: 24- Drying Temperature: 110°C Drying Time: 4hrs Drying Time (Cumulative): 8hrs Maximum Moisture Content: 0.02% Barrel - Zone 1 Temperature: 215 to 235.0°C Barrel - Zone 2 Temperature: 235 to 265.0°C Barrel - Zone 3 Temperature: 235 to 265.0°C Barrel - Zone 4 Temperature: 235 to 265.0°C Nozzle Temperature: 235 to 265.0°C Melt Temperature: 235 to 265.0°C Bed Temperature: 80 to 120.0°C Extruder Pressure: <11MPa
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.