Description

LNP ELCRIN W10001iQ, utilizing iQ upcycling technology, is an unreinforced, non-chlorinated/brominated flame retardant Polybutylene Terephthalate (PBT) injection moldable grade. Added features include PCR content, excellent chemical resistance and UL94V0 flame rating. This grade contains minimum 44% PCR weight content. This is a good candidate for a variety of applications needing a more sustainable FR and PBT solution.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Impact strength, Izod unnotched, ASTM	23.0 °C	550 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 550 J/m	ASTM D 4812 \| 23°C
Elastic modulus	ISO 527 \| 1 mm/min
Elongation	ISO 527 \| yield, 5 mm/min
Flexural modulus	ISO 178 \| 2 mm/min
Flexural strength	ISO 178 \| yield, 2 mm/min
Tensile strength	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	55 - 150 °C Show Supplier Material materials with Heat deflection temperature of 55 - 150 °C
Heat deflection temperature, 0.45 MPa	150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	55 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 55 °C	ASTM D 648 \| 3.2mm, unannealed
Vicat softening temperature	207 °C Show Supplier Material materials with Vicat softening temperature of 207 °C	ASTM D 1525 \| Rate A/120

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		20 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 20 cm³/10min	ISO 1133 \| MVR at 250°C/2.16 kg
Shrinkage	23.0 °C	1.8 % Show Supplier Material materials with Shrinkage of 1.8 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Automotive , Electronics
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 100 to 120.0°C Drying Time: 2 to 4.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 245 to 260.0°C Nozzle Temperature: 230 to 255.0°C Front - Zone 3 Temperature: 240 to 260.0°C Middle - Zone 2 Temperature: 235 to 250.0°C Rear - Zone 1 Temperature: 230 to 240.0°C Hopper Temperature: 40 to 60.0°C Mold Temperature: 40 to 100.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.