Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.54 g/cm³ Show Supplier Material materials with Density of 1.54 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.54 [-] Show Supplier Material materials with Relative density of 1.54 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.09 % Show Supplier Material materials with Water absorption of 0.09 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.7 GPa Show Supplier Material materials with Elastic modulus of 10.7 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.6 % Show Supplier Material materials with Elongation of 1.6 % | ISO 527 | yield, 5 mm/min |
Flexural modulus | 23.0 °C | 9.1 GPa Show Supplier Material materials with Flexural modulus of 9.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 210 MPa Show Supplier Material materials with Flexural strength of 210 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 83 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 83 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 770 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 770 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 139 MPa Show Supplier Material materials with Tensile strength of 139 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ball pressure temperature | 200 °C Show Supplier Material materials with Ball pressure temperature of 200 °C | IEC 60695-10-2 | approximate maximum | |
Coefficient of thermal expansion | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.9E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 203 - 217 °C Show Supplier Material materials with Heat deflection temperature of 203 - 217 °C | ||
Heat deflection temperature, 0.45 MPa | 217 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 217 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ASTM D 648 | 3.2mm, unannealed |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
Dielectric strength | 23.0 °C | 23 kV/mm Show Supplier Material materials with Dielectric strength of 23 kV/mm | ASTM D 149 | in air, 3.2 mm |
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 52 g/10min Show Supplier Material materials with Melt mass-flow rate of 52 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Melt volume-flow rate | 38 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 38 cm³/10min | ISO 1133 | MVR at 250°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.8 % Show Supplier Material materials with Shrinkage, transverse of 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Small Appliance, Personal Care | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |