LNP™ ELCRIN™ EXL8483RCC

Want to keep this datasheet? Save it now in your required format

Description

LNP ELCRIN EXL8483RCC is a Post-Consumer Recycled (PCR) resin based on PC/siloxane copolymer. Added features of this material include: medium flow, colorable and minimum 75% post-consumer recycle content. Developed for applications that require improved aesthetics and wider color space to overcome restricted color space of traditional PCR grades.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Automotive

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³	ISO 1183
Relative density	23.0 °C	1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.16 % Show Supplier Material materials with Water absorption of 0.16 %	ASTM D 570 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	6.2 % Show Supplier Material materials with Elongation of 6.2 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	95 MPa Show Supplier Material materials with Flexural strength of 95 MPa	ISO 178 \| 2 mm/min
Impact strength, Charpy notched	23.0 °C	37 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 37 kJ/m²	ISO 179/1eA \| V-notch Edgew 80103 sp=62mm, 23°C
Impact strength, Izod notched	23.0 °C	32 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 32 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	750 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 750 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	137 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 137 kJ/m²	ISO 180/1U \| unnotched 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	1730 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1730 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	62 MPa Show Supplier Material materials with Tensile strength of 62 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	6.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.6E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Coefficient of thermal expansion, transverse	23.0 °C	7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.5E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature		124 - 139 °C Show Supplier Material materials with Heat deflection temperature of 124 - 139 °C
Heat deflection temperature, 0.45 MPa		139 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 139 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		144 °C Show Supplier Material materials with Vicat softening temperature of 144 °C	ISO 306 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		15 g/10min Show Supplier Material materials with Melt mass-flow rate of 15 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Melt volume-flow rate		13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg
Shrinkage	23.0 °C	0.8 % Show Supplier Material materials with Shrinkage of 0.8 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.8 % Show Supplier Material materials with Shrinkage, transverse of 0.8 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Heavy Vehicles, Data Transfer, Audio, Wireless Communications
Availability	Europe,Asia,Americas
Processing methods	Melt Temperature: 295 to 315.0°C Nozzle Temperature: 290 to 310.0°C Front - Zone 3 Temperature: 295 to 315.0°C Middle - Zone 2 Temperature: 280 to 305.0°C Rear - Zone 1 Temperature: 270 to 295.0°C Mold Temperature: 70 to 95.0°C Drying Temperature: 120°C Drying Time (Cumulative): 3 to 4.0hrs Maximum Moisture Content: 0.02% Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.